Electrical properties of amorphous Zn–Sn–O thin films depending on composition and post-deposition annealing temperature near crystallization temperature

Abstract

This study investigated the crystallization and electrical properties of atomic layer deposited Zn–Sn–O (ZTO) thin films. Also, the optimum composition ratio that can provide thermal stability and good device performance for the ZTO thin film through high-temperature annealing was examined. As a result, it was confirmed that the highest crystallization temperature was ∼700 °C in Sn 42–66 at%, and the best device performance was observed at Sn 42 at%. This conclusion is attributed to the difference in the shallow donor-level energy distribution of the Sn-related and the Zn-related oxygen vacancies. Furthermore, the higher the annealing temperature below the crystallization temperature, the better the mobility, presumed to be caused by decreased defect density. However, a sudden decrease in device performance was observed in the region above the crystallization temperature due to the formation of grain boundaries and related defects. Therefore, the optimal Sn concentration to provide thermal stability and good device performance of the ZTO thin film was approximately 42 at%, where promising device performances were achieved, including a carrier mobility of 25.5 cm2 V−1 s−1, a subthreshold swing of 0.30 V decade−1, and a threshold voltage of −0.52 V.

Graphical abstract: Electrical properties of amorphous Zn–Sn–O thin films depending on composition and post-deposition annealing temperature near crystallization temperature

Supplementary files

Article information

Article type
Paper
Submitted
30 noy 2022
Accepted
17 apr 2023
First published
17 apr 2023

J. Mater. Chem. C, 2023,11, 8254-8262

Electrical properties of amorphous Zn–Sn–O thin films depending on composition and post-deposition annealing temperature near crystallization temperature

W. Kim, S. Kang, Y. Lee, S. Mun, J. Choi, S. Lee and C. S. Hwang, J. Mater. Chem. C, 2023, 11, 8254 DOI: 10.1039/D2TC05090K

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements