Abstract

Ag(Nb0.8Ta0.2)O3 is used here as a model system to shed light on the nature of the low temperature phase behavior of the unsubstituted parent compound AgNbO3, which is an important material for high-power energy storage applications. The three dielectric anomalies previously identified as M1 ↔ M2, Tf and M2 ↔ M3 transitions in AgNbO3 ceramics are found to be intimately related to the polarization the behavior of the B-site cations. In particular, the M1 ↔ M2 transition is found to involve the disappearance of original ferroelectric polar structure in the M1 phase. Analysis of weak-field and strong field hysteresis loops in the M2 region below Tf suggests the presence of a weakly-polar structure exhibiting antipolar behavior (i.e., a non-compensated antiferroelectric), which can be considered as ferrielectric (FIE). Modeling of the permittivity data using the Curie–Weiss law indicates that the Curie temperature is close to the freezing temperature, Tf, which can be regarded as the Curie point of the FIE phase. Substitution by Ta5+ in this system enhances the stability of the weakly polar/antiferroelectric state, giving rise to an increased energy storage density of 3.7 J cm−3 under an applied field of 27 MV m−1, one of the highest values ever reported for a dielectric ceramic. Furthermore, the energy storage capability remains approximately constant at around 3 J cm−3 up to 100 °C, at an applied field of 22 MV m−1.

Graphical abstract: Phase transitions in tantalum-modified silver niobate ceramics for high power energy storage

Article information

Article type
Paper
Submitted
19 okt 2018
Accepted
09 dek 2018
First published
10 dek 2018

J. Mater. Chem. A, 2019,7, 834-842

Phase transitions in tantalum-modified silver niobate ceramics for high power energy storage

Y. Tian, L. Jin, Q. Hu, K. Yu, Y. Zhuang, G. Viola, I. Abrahams, Z. Xu, X. Wei and H. Yan, J. Mater. Chem. A, 2019, 7, 834 DOI: 10.1039/C8TA10075F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements