Charge storage mechanism and degradation of P2-type sodium transition metal oxides in aqueous electrolytes

Abstract

Few transition metal oxides exhibit sufficient stability for aqueous ion intercalation from neutral pH electrolytes for low-cost aqueous Na+ batteries and battery-type desalinators. P2 layered Na+ manganese-rich oxides have high theoretical capacities and voltages for Na+ storage and are extensively investigated for non-aqueous Na+ batteries. However, the charge storage mechanism and factors controlling interlayer chemistry and redox behavior of these materials in aqueous electrolytes have not been determined. Here, we take a significant step in establishing their aqueous electrochemical behavior by investigating a series of P2 oxides that exhibit a range of stability in water and ambient air: Na0.62Ni0.22Mn0.66Fe0.10O2 (NaNMFe), Na0.61Ni0.22Mn0.66Co0.10O2 (NaNMCo), Na0.64Ni0.22Mn0.66Cu0.11O2 (NaNMCu), and Na0.64Mn0.62Cu0.31O2 (NaMCu). Depending on the transition metal composition and potential, all materials exhibit significant irreversible Na+ loss during the first anodic cycle followed by water intercalation into the interlayer. The presence of water causes conversion into birnessite-like phases and microscopic exfoliation of the particles. The interlayer affinity for water is primarily driven by the Na+ content, which can be tuned by the transition metal composition and the maximum anodic potential during electrochemical cycling. The interlayer water affects the reversible capacity and cycling stability of the oxides, with the highest reversible capacity (∼40 mA h g−1 delivered in ∼30 minutes) obtained with NaNMCo. These results present the first studies on the structural effects of aqueous electrochemistry in P2 oxides, highlight the significant differences in the electrochemical behavior of P2 oxides in aqueous vs. non-aqueous electrolytes, and provide guidance on how to use the transition metal chemistry to tune their aqueous charge storage behavior.

Graphical abstract: Charge storage mechanism and degradation of P2-type sodium transition metal oxides in aqueous electrolytes

Supplementary files

Article information

Article type
Paper
Submitted
28 avq 2018
Accepted
09 okt 2018
First published
09 okt 2018

J. Mater. Chem. A, 2018,6, 22266-22276

Author version available

Charge storage mechanism and degradation of P2-type sodium transition metal oxides in aqueous electrolytes

S. Boyd, R. Dhall, James M. LeBeau and V. Augustyn, J. Mater. Chem. A, 2018, 6, 22266 DOI: 10.1039/C8TA08367C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements