Reduction of thermal conductivity through nanostructuring enhances the thermoelectric figure of merit in Ge1−xBixTe

Abstract

A promising thermoelectric figure of merit, zT, of ∼1.3 at 725 K was obtained in high quality crystalline ingots of Ge1−xBixTe. The substitution of Bi3+ in a Ge2+ sublattice of GeTe significantly reduces the excess hole concentration due to the aliovalent donor dopant nature of Bi3+. Reduction in carrier density optimizes electrical conductivity, and subsequently enhances the Seebeck coefficient in Ge1−xBixTe. More importantly, a low lattice thermal conductivity of ∼1.1 W m−1 K−1 for Ge0.90Bi0.10Te was achieved, which is due to the collective phonon scattering from meso-structured grain boundaries, nano-structured precipitates, nano-scale defect layers, and solid solution point defects. We have obtained a reasonably high mechanical stability for the Ge1−xBixTe samples. The measured Vickers microhardness value of the high performance sample is ∼165 HV, which is comparatively higher than that of state-of-the-art thermoelectric materials, such as PbTe, Bi2Te3, and Cu2Se.

Graphical abstract: Reduction of thermal conductivity through nanostructuring enhances the thermoelectric figure of merit in Ge1−xBixTe

Supplementary files

Article information

Article type
Research Article
Submitted
31 okt 2015
Accepted
17 noy 2015
First published
18 noy 2015

Inorg. Chem. Front., 2016,3, 125-132

Reduction of thermal conductivity through nanostructuring enhances the thermoelectric figure of merit in Ge1−xBixTe

S. Perumal, S. Roychowdhury and K. Biswas, Inorg. Chem. Front., 2016, 3, 125 DOI: 10.1039/C5QI00230C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements