Inkjet-printed all solid-state electrochromic devices based on NiO/WO3 nanoparticle complementary electrodes

Abstract

Nanostructured thin films are important in the fields of energy conversion and storage. In particular, multi-layered nanostructured films play an important role as a part of the energy system for energy saving applications in buildings. Inkjet printing is a low-cost and attractive technology for patterning and deposition of multi-layered nanostructured materials on various substrates. However, it requires the development of a suitable ink formulation with optimum viscosity, surface tension and evaporation rate for various materials. In this study, a versatile ink formulation was successfully developed to prepare NiO and WO3 nanostructured films with strong adhesion to ITO coated glass using inkjet printing for energy saving electrochromic applications. We achieved a high performance electrochromic electrode, producing porous and continuous electrochromic films without aggregation. The NiO film with 9 printed layers exhibits an optical modulation of 64.2% at 550 nm and a coloration efficiency (CE) of 136.7 cm2 C−1. An inkjet-printed complementary all solid-state device was assembled, delivering a larger optical modulation of 75.4% at 633 nm and a higher CE of 131.9 cm2 C−1 among all solid-state devices. The enhanced contrast is due to the printed NiO film that not only performs as an ion storage layer, but also as a complementary electrochromic layer.

Graphical abstract: Inkjet-printed all solid-state electrochromic devices based on NiO/WO3 nanoparticle complementary electrodes

Supplementary files

Article information

Article type
Paper
Submitted
09 okt 2015
Accepted
13 noy 2015
First published
16 noy 2015

Nanoscale, 2016,8, 348-357

Inkjet-printed all solid-state electrochromic devices based on NiO/WO3 nanoparticle complementary electrodes

G. Cai, P. Darmawan, M. Cui, J. Chen, X. Wang, A. L. Eh, S. Magdassi and P. S. Lee, Nanoscale, 2016, 8, 348 DOI: 10.1039/C5NR06995E

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements