Issue 34, 2015

Multi-scale thermal stability of niobate-based lead-free piezoceramics with large piezoelectricity

Abstract

Growing environmental concerns are pushing the development of lead-free piezoceramics with both outstanding piezoelectric properties and reasonable thermal stability. Herein, we realized a large piezoelectric coefficient d33 of 430 pC N−1 in 0.96(K0.4Na0.6)(Nb0.96Sb0.04)O3–0.04Bi0.5K0.5Zr0.85Sn0.15O3 (KNNS–BKZS) polycrystals by constructing a rhombohedral–tetragonal (R–T) phase boundary. Investigations of the in situ thermal stability of the piezoelectric properties on multiple scales reveal that the micro-scale piezoelectric response is much more stable compared to the macro-scale response, indicating the significant role of extrinsic contributions from domain wall movements. These findings demonstrate the relationship between multi-scale properties and domain structures, revealing that the high piezoelectricity is attributed to nano-domains at the R–T phase boundary.

Graphical abstract: Multi-scale thermal stability of niobate-based lead-free piezoceramics with large piezoelectricity

Article information

Article type
Communication
Submitted
13 may 2015
Accepted
14 iyl 2015
First published
14 iyl 2015

J. Mater. Chem. C, 2015,3, 8780-8787

Multi-scale thermal stability of niobate-based lead-free piezoceramics with large piezoelectricity

J. Zhou, K. Wang, F. Yao, T. Zheng, J. Wu, D. Xiao, J. Zhu and J. Li, J. Mater. Chem. C, 2015, 3, 8780 DOI: 10.1039/C5TC01357G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.