Abstract

Porous RhoZMOF is a negatively charged zeolite-like MOF material susceptible to post-synthesis modification by an ion-exchange process replacing as-synthesized organic cations with transition metals. This material exhibiting open transition metal sites is a very attractive candidate for industrial applications related to clean energy technologies, like electrochemistry and gas storage. In the present work, partial or total Co2+, Ni2+ and Cu2+ inclusions have been successfully carried out in the RhoZMOF structure by ion-exchange treatment. Particularly, complete exchange of HDMA+ with Co2+ could be reached at room temperature after 12 h of contact time. For Cu2+ exchange, a rapid transformation of the RhoZMOF structure into a new Cu-rich, crystalline and practically non-porous phase was observed at room temperature; its appearance can be avoided and the desired structure can be preserved when ion-exchange treatment is carried out at −20 °C for 6 h, reaching a partial ion-exchange degree of 30%. Moreover, for Ni2+ ion-exchange treatment at 25 and 0 °C, a covering of an amorphous Ni-rich organometallic phase over the crystals was detected by SEM analysis; its appearance can be prevented by reducing the amount of HDMA+ in the media by developing the ion-exchange process in two steps: exchanging HDMA+ with Na+ and Na+ with Ni2+. The results provide a post-synthesis modification route for obtaining porous MOF materials containing open transition metal sites accessible for redox catalysis and selective gas adsorption.

Graphical abstract: Transition metal inclusion in RhoZMOF materials

Supplementary files

Article information

Article type
Paper
Submitted
07 iyl 2014
Accepted
22 sen 2014
First published
22 sen 2014

CrystEngComm, 2015,17, 338-343

Author version available

Transition metal inclusion in RhoZMOF materials

G. Calleja, C. Martos, G. Orcajo, J. A. Botas and J. A. Villajos, CrystEngComm, 2015, 17, 338 DOI: 10.1039/C4CE01401D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements