Porosity modulation of activated ZIF-templated carbons via compaction for hydrogen and CO2 storage applications

Abstract

The mechanical stability of activated ZIF-templated carbon materials, prepared via liquid impregnation and chemical vapour deposition (CVD) methods, was investigated by compaction at various pressures (compaction loads of 5 and 10 tonnes equivalent to 370 and 740 MPa, respectively). Compaction at 5 tonnes (370 MPa) was, unusually, found to increase the textural properties (surface area and pore volume) and gas (hydrogen and CO2) uptake capacity. In particular, compaction at 5 tonnes resulted in higher micropore surface area and pore volume, and an overall rise in the total surface area and pore volume. Compaction resulted in an improved gas uptake capacity of 6.5 wt% hydrogen (at −196 °C and 20 bar) and 2.4 mmol g−1 of CO2 (at 25 °C and 1 bar) for an activated ZIF-templated carbon compacted at 5 tonnes following preparation via liquid impregnation and carbonisation at 900 °C. When the carbon was compacted at 10 tonnes (740 MPa), the hydrogen and CO2 uptake was marginally lower at 5.7 wt% and 2.2 mmol g−1, respectively, compared to the uptake of 6.2 wt% hydrogen and 2.0 mmol g−1 CO2 for the equivalent non-compacted sample. More importantly, increase in packing density after compaction resulted in up to 70% improvement in volumetric hydrogen uptake, which reached 42.3 g l−1 at −196 °C and 20 bar, much higher than that for conventional activated carbons, and one of the highest values ever reported under these conditions. The genesis of the increase in textural properties after compaction appears to be linked to the pore size distribution and mechanical stability of the activated ZIF-templated carbons and their structural rearrangement under compaction, especially at a load of 5 tonnes that results in an increase in the proportion of microporosity.

Graphical abstract: Porosity modulation of activated ZIF-templated carbons via compaction for hydrogen and CO2 storage applications

Article information

Article type
Paper
Submitted
28 ربيع الأول 1435
Accepted
05 رجب 1435
First published
07 رجب 1435

J. Mater. Chem. A, 2014,2, 10960-10968

Porosity modulation of activated ZIF-templated carbons via compaction for hydrogen and CO2 storage applications

A. Almasoudi and R. Mokaya, J. Mater. Chem. A, 2014, 2, 10960 DOI: 10.1039/C4TA00530A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements