Mitigating magnetic frustration to improve single-crystalline nonstoichiometric Li1.06Ni0.90Mn0.04O2 for lithium-ion batteries

Abstract

Single-crystalline Co-free layered nickel-rich oxide LiNi1−xMnxO2 (x ≤ 0.1) is an appealing cathode material but suffers from significant structural degradation that correlates with the Li+/Ni2+ cation mixing induced by the magnetic frustration. In this study, we propose a molten salt-assisted synthesis and a Li-refeeding strategy to prepare a single-crystalline slightly Li-rich Li1.06Ni0.90Mn0.04O2 cathode material. A small amount of lithium doping into the transition metal layer increases the average valence of Ni and Mn, and reduces the magnetic frustration, as evidenced by electron energy loss spectroscopy and superconducting quantum interference device. Benefiting from mitigated magnetic frustration, the single-crystalline slightly Li-rich Li1.06Ni0.90Mn0.04O2 delivers a high specific capacity of 214.8 mA h g−1 at 0.1 C, and a remarkable capacity retention of 93.4% after 100 cycles at 5C in a coin cell, and achieves a superior long-term stability of 400 cycles with 79.4% capacity retention at 2C in a 362.9 mA h pouch full cell. The results validate the mitigation of magnetic frustration by tuning the Li stoichiometry to reinforce the structural stability for the design of better Co-free nickel-rich oxide cathode materials.

Graphical abstract: Mitigating magnetic frustration to improve single-crystalline nonstoichiometric Li1.06Ni0.90Mn0.04O2 for lithium-ion batteries

Supplementary files

Article information

Article type
Paper
Submitted
29 ذو القعدة 1445
Accepted
18 محرم 1446
First published
20 محرم 1446

J. Mater. Chem. A, 2024,12, 23454-23460

Mitigating magnetic frustration to improve single-crystalline nonstoichiometric Li1.06Ni0.90Mn0.04O2 for lithium-ion batteries

G. Ding, S. Wang, X. Huang, Q. Zhao, Y. Peng, Z. Wu, N. Jiang, K. Liu, Y. Zhang, Z. Hou, W. Yang, M. Yu, F. Liu and F. Cheng, J. Mater. Chem. A, 2024, 12, 23454 DOI: 10.1039/D4TA03933E

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements