High piezoelectricity induced by lattice distortion and domain realignment in Li2CO3-added lead-based ceramics

Abstract

The 0.2Pb(Ni1/3Nb2/3)O3–0.1Pb(Zn1/3Nb2/3)O3–0.7Pb(Zr0.46Ti0.54)O3 + xwt% Li2CO3 ceramics were synthesized by the solid-state reaction method. After doping Li+ ions into the ceramics, the [BO6] oxygen octahedra stretch along the direction of the spontaneous polarization (Ps), which increases the Ps and improves the internal contribution to the piezoelectric properties. The calculated Ps and measured Ps have the same trend with increasing the Li2CO3 content from 0.0 to 0.6 wt%, confirming that the Rietveld refinement results are reliable. The local structural distortion is observed by scanning transmission electron microscopy (STEM). Meanwhile, the increased relaxation promotes the formation of short-ordered nanoscale domains, making the domain rotation and the domain-wall motion easier, thus improving the external contribution to the piezoelectric properties. The ratio of extrinsic contribution increases as the electric field increases. The nanoscale domains have lower activation energy of domain wall (Ea) movement than the micron-scale domains.

Graphical abstract: High piezoelectricity induced by lattice distortion and domain realignment in Li2CO3-added lead-based ceramics

Supplementary files

Article information

Article type
Paper
Submitted
13 ربيع الأول 1445
Accepted
01 جمادى الأولى 1445
First published
02 جمادى الأولى 1445

J. Mater. Chem. A, 2023,11, 25945-25954

High piezoelectricity induced by lattice distortion and domain realignment in Li2CO3-added lead-based ceramics

H. Chen, Y. Xie, J. Xi, W. Zhuang, W. Wang, J. Xing, H. Liu and J. Zhu, J. Mater. Chem. A, 2023, 11, 25945 DOI: 10.1039/D3TA05899A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements