Plasma-enhanced atomic layer deposition of nickel and cobalt phosphate for lithium ion batteries

Abstract

A plasma-enhanced ALD process has been developed to deposit nickel phosphate. The process combines trimethylphosphate (TMP) plasma with oxygen plasma and nickelocene at a substrate temperature of 300 °C. Saturation at a growth per cycle of approximately 0.2 nm per cycle is observed for both the TMP plasma and nickelocene, while a continuous decrease in the growth per cycle is found for the oxygen plasma. From ERD, a stoichiometry of Ni3(P0.8O3.1)2 is measured, but by adding additional oxygen plasma after nickelocene, the composition of Ni3(P0.9O3.7)2 becomes even closer to stoichiometric Ni3(PO4)2. The as-deposited layer resulting from the process without the additional oxygen plasma is amorphous but can be crystallized into Ni2P or crystalline Ni3(PO4)2 by annealing under a hydrogen or helium atmosphere, respectively. The layer deposited with the additional oxygen plasma shows two X-ray diffraction peaks indicating the formation of crystalline Ni3(PO4)2 already during the deposition. The resulting PE-ALD deposited nickel phosphate layers were then electrochemically studied and compared to PE-ALD cobalt and iron phosphate. All phosphates need electrochemical activation at low potential first, after which reversible redox reactions are observed at a potential of approximately 2.5 V vs. Li+/Li. A relatively high capacity and good rate behavior are observed for both nickel and cobalt phosphate, which are thought to originate from either a conversion type reaction or an alloying reaction.

Graphical abstract: Plasma-enhanced atomic layer deposition of nickel and cobalt phosphate for lithium ion batteries

Supplementary files

Article information

Article type
Paper
Submitted
04 ربيع الأول 1443
Accepted
08 جمادى الأولى 1443
First published
17 جمادى الأولى 1443

Dalton Trans., 2022,51, 2059-2067

Plasma-enhanced atomic layer deposition of nickel and cobalt phosphate for lithium ion batteries

L. Henderick, R. Blomme, M. Minjauw, J. Keukelier, J. Meersschaut, J. Dendooven, P. Vereecken and C. Detavernier, Dalton Trans., 2022, 51, 2059 DOI: 10.1039/D1DT03417K

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements