Structural evolution and microwave dielectric properties of a novel Li3Mg2−x/3Nb1−2x/3TixO6 system with a rock salt structure

Abstract

In this study, the Li3Mg2−x/3Nb1−2x/3TixO6 (0 ≤ x ≤ 0.6) solid solution was designed and synthesized by the solid-state reaction method. The ordering degree decreased with the increasing Ti content, and the ordered orthorhombic superstructure was continuously transformed to the disordered MgO-like cubic subcell structure with no other impure phase observed in the range of 0.12 ≤ x ≤ 0.38. During the phase transition process, the ordered domains were found in orthorhombic superstructures by TEM images. According to the variation of Raman patterns, the B1g, B2g and B3g vibration modes which derive from Nb–Nb repulsive force in 8a sites were assigned to the band at 480 cm−1. The relative densities and dielectric constants showed a similar nonlinear variation with the increase of Ti content. However, as x increased from 0 to 0.4, the phase transition contributed to the huge improvement of Q × f values from 82 338 GHz to 125 357 GHz (about 50%), but it also led to a slight decrease in the temperature coefficient of resonant frequency (τf). After being sintered at 1260 °C for 6 h, the Li3Mg1.87Nb0.73Ti0.40O6 (x = 0.4) ceramics showed excellent microwave properties: εr = 15.09, Q × f = 125 357 GHz and τf = −31.7 ppm °C−1.

Graphical abstract: Structural evolution and microwave dielectric properties of a novel Li3Mg2−x/3Nb1−2x/3TixO6 system with a rock salt structure

Supplementary files

Article information

Article type
Research Article
Submitted
27 ذو الحجة 1439
Accepted
06 صفر 1440
First published
07 صفر 1440

Inorg. Chem. Front., 2018,5, 3113-3125

Structural evolution and microwave dielectric properties of a novel Li3Mg2−x/3Nb1−2x/3TixO6 system with a rock salt structure

X. Zhang, B. Tang, Z. Fang, H. Yang, Z. Xiong, L. Xue and S. Zhang, Inorg. Chem. Front., 2018, 5, 3113 DOI: 10.1039/C8QI00956B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements