Template-free synthesis of mesoporous manganese oxides with catalytic activity in the oxygen evolution reaction

Abstract

Porous manganese carbonate was obtained via solvothermal synthesis using ethanol and urea. The manganese carbonate was subsequently used as a precursor to synthesise mesoporous manganese oxides via thermal treatments at three various temperatures. X-ray diffraction and Extended X-ray Absorption Fine Structure (EXAFS) results shows that γ-MnO2 is synthesised at 380 and 450 °C while Mn2O3 is produced at the annealing temperature of 575 °C. X-ray absorption spectra show that γ-MnO2 converts completely to Mn2O3 after annealing over the 450–575 °C range. The oxides obtained at 380 °C and 450 °C possess extremely high specific surface area, which is of interest for catalytic applications. The oxides were investigated as electrocatalysts for the oxygen evolution reaction; the oxide prepared at the lowest annealing temperature was found to be the optimum catalyst with an overpotential of 427 ± 10 mV at a current density of 10 mA cm−2, normalised by the geometric area. The improved catalytic activity was related to the presence of defect-rich and highly porous manganese dioxide at the lowest annealing temperature.

Graphical abstract: Template-free synthesis of mesoporous manganese oxides with catalytic activity in the oxygen evolution reaction

Supplementary files

Article information

Article type
Paper
Submitted
13 جمادى الأولى 1438
Accepted
14 رجب 1438
First published
15 رجب 1438

Sustainable Energy Fuels, 2017,1, 780-788

Template-free synthesis of mesoporous manganese oxides with catalytic activity in the oxygen evolution reaction

S. Lian, M. P. Browne, C. Domínguez, S. N. Stamatin, H. Nolan, G. S. Duesberg, M. E. G. Lyons, E. Fonda and P. E. Colavita, Sustainable Energy Fuels, 2017, 1, 780 DOI: 10.1039/C7SE00086C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements