Tunable structural and magnetic properties of chemically synthesized dual-phase Co2NiGa nanoparticles

Abstract

We report the structural and magnetic properties of chemically synthesized dual-phase Co2NiGa shape memory Heusler nanoparticles (NPs). Rietveld analysis of the X-ray diffraction (XRD) data reveals a dual-phase structure for all studied Co2NiGa NPs: the B2 ordered cubic austenite (β) and the tetragonal (γ or martensite β′) phases. We find that the fraction of the tetragonal γ-phase and magnetic properties of NPs consisting of β + γ phases prepared using a heating rate of 0.5 K min−1 can be tuned by varying the Ni-content. Higher saturation magnetization and Curie temperature are observed for Co2NiGa NPs with a higher fraction of the γ-phase. Dual-phase β + γ Co2NiGa NPs exhibit the highest Curie temperature (1153 K) of all known Heusler NPs. Furthermore, the martensite β′-phase is found to coexist with the β-phase for NPs synthesized using a higher heating rate of 2 K min−1. Co2NiGa NPs of mixed β + β′ phase are paramagnetic at room temperature and exhibit low magnetization due to the presence of the martensite phase. High temperature XRD measurements of Co2NiGa NPs with β + β′ phases confirm their irreversible phase transition of the β-phase starting at a temperature of 837 K and the structural stability of the tetragonal β′-phase. The developed new synthetic method makes it possible to fabricate Co2NiGa NPs with structure and properties tailored for high temperature magnetic shape memory devices at the nanoscale.

Graphical abstract: Tunable structural and magnetic properties of chemically synthesized dual-phase Co2NiGa nanoparticles

Supplementary files

Article information

Article type
Paper
Submitted
23 رجب 1437
Accepted
30 رمضان 1437
First published
30 رمضان 1437

J. Mater. Chem. C, 2016,4, 7241-7252

Tunable structural and magnetic properties of chemically synthesized dual-phase Co2NiGa nanoparticles

C. Wang, A. A. Levin, S. Fabbrici, L. Nasi, J. Karel, J. Qian, C. E. Viol Barbosa, S. Ouardi, F. Albertini, W. Schnelle, H. Borrmann, G. H. Fecher and C. Felser, J. Mater. Chem. C, 2016, 4, 7241 DOI: 10.1039/C6TC01757F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements