Solution processable formation of a few nanometer thick-disordered overlayer on the surface of open-ended TiO2 nanotubes

Abstract

Herein, we designed vertically aligned TiO2 nanotube arrays, in which a very thin disordered overlayer approximately a few nm thick was formed via a room-temperature solution process. At the optimal overlayer thickness, the TiO2 nanotube arrays yielded a photocurrent density of up to ∼1.75 mA cm−2 at 1.23 V vs. RHE, approximately twice that of the pristine one.

Graphical abstract: Solution processable formation of a few nanometer thick-disordered overlayer on the surface of open-ended TiO2 nanotubes

Supplementary files

Article information

Article type
Communication
Submitted
18 ذو الحجة 1437
Accepted
01 صفر 1438
First published
02 صفر 1438

Chem. Commun., 2016,52, 13807-13810

Solution processable formation of a few nanometer thick-disordered overlayer on the surface of open-ended TiO2 nanotubes

S. W. Kwon, M. Ma, M. J. Jeong, K. Zhang, S. J. Kim and J. H. Park, Chem. Commun., 2016, 52, 13807 DOI: 10.1039/C6CC07611D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements