Abstract

The inverted perovskite solar cell fabricated using a two-step method exhibited the highest FF of 0.85 and good efficiency of 18% based on CH3NH3PbI3. A small amount of H2O was added into PbI2/DMF to make a homogenous precursor solution. A high quality PbI2 film with full coverage was formed on a PEDOT:PSS surface by spin coating of the homogeneous PbI2 precursor solution. The perovskite film fabricated from the high quality PbI2 film is highly pure, smooth and very dense even without any pinhole. The champion cell achieves a remarkable fill factor (FF) of 0.85, which is the highest value reported in perovskite solar cells. The FF value is also very reproducible with less than 10% deviation for 50 cells. The cell exhibits no current hysteresis and is stable under both dark and illumination conditions in dry and inert atmospheres. The results not only provide a strategy to fabricate high efficiency inverted perovskite solar cells but also reveal how the water additive in the PbI2/DMF solution may affect the properties of PbI2 and therefore the perovskite film prepared using the two-step method and the overall photovoltaic performance of the corresponding inverted solar cell.

Graphical abstract: High efficiency stable inverted perovskite solar cells without current hysteresis

Supplementary files

Article information

Article type
Paper
Submitted
07 جمادى الأولى 1436
Accepted
28 رمضان 1436
First published
11 شوال 1436

Energy Environ. Sci., 2015,8, 2725-2733

Author version available

High efficiency stable inverted perovskite solar cells without current hysteresis

C. Wu, C. Chiang, Z. Tseng, Md. K. Nazeeruddin, A. Hagfeldt and M. Grätzel, Energy Environ. Sci., 2015, 8, 2725 DOI: 10.1039/C5EE00645G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements