Atomic-scale observation of rotational misorientation in suspended few-layer graphene sheets

Abstract

Single or few-layer graphene (FLG) sheets offer extraordinary electronic, thermal and mechanical properties and are expected to find a variety of applications. Fully exploiting the properties of graphene will require a method for the production of high-quality graphene sheets (almost pristine graphene) in large quantities. In this regard, we report a two-step method for obtaining a homogenous colloidal suspension of single or FLG sheets up to 0.15 mg ml−1 in N,N-dimethylformamide solution. The graphene nanostructures are directly imaged using a high-resolution transmission electron microscope (HRTEM) operated at 200 kV with a point resolution of 0.16 nm. We observed rotational misorientation within the flake in the HRTEM images of 2, 4 and 6 layers of graphene sheets, giving rise to Moiré patterns. By filtering in the frequency domain using a Fourier transform, we reconstruct the graphene lattice of each sheet and determine the relative rotation between consecutive graphene layers up, to six separate sheets. Direct evidence is obtained for FLG sheets with packing that is different to the standard AB Bernal packing of bulk graphite. Furthermore, we observed periodic ripples in suspended graphene sheets in our TEM measurements. Electrostatic force microscopy was used to characterize the electric potential distribution on the surface of FLG sheets on SiO2/Si substrates in ambient conditions. The FLG sheets were found to exhibit a conducting nature with small potential variations on the surface.

Graphical abstract: Atomic-scale observation of rotational misorientation in suspended few-layer graphene sheets

Article information

Article type
Paper
Submitted
21 رمضان 1430
Accepted
24 ذو القعدة 1430
First published
21 محرم 1431

Nanoscale, 2010,2, 700-708

Atomic-scale observation of rotational misorientation in suspended few-layer graphene sheets

M. K. Singh, E. Titus, G. Gonçalves, P. A. A. P. Marques, I. Bdikin, A. L. Kholkin and J. J. A. Gracio, Nanoscale, 2010, 2, 700 DOI: 10.1039/B9NR00256A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements