Engineering defects in 2D g-C3N4 for wideband, efficient electromagnetic absorption at elevated temperature

Abstract

Metal-free 2D nanomaterials such as graphitic carbon nitride (g-C3N4) nanosheets have attracted enormous attention due to their ultralow mass density, excellent chemical stability, high specific surface area, unique electronic structure and permittivity. However, the electromagnetic (EM) wave absorption performance of g-C3N4 cannot satisfy the requirements for addressing the ever-increasing occurrence of EM pollution. Herein, we demonstrate that the creation of pores in g-C3N4 nanosheets, combined with subsequent doping with phosphorus (P) and sulphur (S) atoms, give rise to a continuous frequency dispersive behaviour along with an enhanced conductive loss capability. As a result, the S/P-doped nanoporous g-C3N4 exhibit an efficient EM absorption over a wide frequency region (e.g., 6.0 GHz of >90% of absorption effectiveness at a sample thickness of 1.8 mm) at elevated temperatures (e.g., >4.0 GHz of >90% of absorption effectiveness at a thickness of 1.2 mm at 150 °C). Overall, our results reported in this work unmask new principles by which metal-free 2D nanomaterials can be modified to enable a significant enhancement in their EM absorption performance.

Graphical abstract: Engineering defects in 2D g-C3N4 for wideband, efficient electromagnetic absorption at elevated temperature

Article information

Article type
Paper
Submitted
02 ኤፕሪ 2021
Accepted
13 ሜይ 2021
First published
13 ሜይ 2021

J. Mater. Chem. A, 2021,9, 19710-19718

Engineering defects in 2D g-C3N4 for wideband, efficient electromagnetic absorption at elevated temperature

H. Lv, X. Zhou, G. Wu, U. I. Kara and X. Wang, J. Mater. Chem. A, 2021, 9, 19710 DOI: 10.1039/D1TA02785A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements