Solution-processed solar-blind deep ultraviolet photodetectors based on strongly quantum confined ZnS quantum dots

Abstract

Solar-blind deep ultraviolet (DUV) photodetectors (PDs) have promising applications in a variety of fields due to the zero background under sun or room illumination. As almost all solar-blind DUV PDs are fabricated based on materials prepared by expensive high temperature and vacuum methods, therefore, solution processed devices are highly desirable for large area, flexible and arrayed applications. Here, we demonstrated that solar-blind DUV PDs can be fabricated using colloidal ZnS quantum dots (QDs). In order to synthesize ZnS QDs with a bandgap in the solar-blind region, a new synthesis was developed. The new method produced monodispersed and strongly quantum confined ZnS QDs with an exciton peak at 265 nm. Solar-blind DUV PDs were fabricated via spin coating and ligand exchange. The ZnS QD solar-blind DUV PDs showed a fast response (Tr = 0.35 s, Td = 0.07 s) and good responsivity (∼0.1 mA W−1) and the performance was comparable to other solar-blind DUV PDs based on some traditional wide bandgap semiconductor materials. The response of the ZnS QD PDs was found to be dominated by the drift of the photogenerated carriers, as the ZnS QD thin film was insensitive to their surface states.

Graphical abstract: Solution-processed solar-blind deep ultraviolet photodetectors based on strongly quantum confined ZnS quantum dots

Supplementary files

Article information

Article type
Paper
Submitted
09 ኦገስ 2018
Accepted
14 ሴፕቴ 2018
First published
17 ሴፕቴ 2018

J. Mater. Chem. C, 2018,6, 11266-11271

Solution-processed solar-blind deep ultraviolet photodetectors based on strongly quantum confined ZnS quantum dots

Y. Xia, G. Zhai, Z. Zheng, L. Lian, H. Liu, D. Zhang, J. Gao, T. Zhai and J. Zhang, J. Mater. Chem. C, 2018, 6, 11266 DOI: 10.1039/C8TC03977A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements