One-pot synthesis of self-supported hierarchical urchin-like Ni3S2 with ultrahigh areal pseudocapacitance

Abstract

Recently, nickel sulfides have been widely investigated as an electrode material for pseudocapacitors. Among them, self-supported nickel sulfides have been intensively studied; yet, their structures are rather limited to nanosheet or nanorod arrays. Herein, a facile one-step hydrothermal method was developed to synthesize self-supported Ni3S2 on a Ni foam substrate with an urchin-like hierarchical structure consisting of nanowire subunits with a diameter of about 20–30 nm, thus combining the advantages of both hierarchical and self-supported structures. Because of this unique structure, when the sample was applied as an electrode for supercapacitors, it demonstrated an ultrahigh areal capacitance of 21.54 F cm−2 at a current rate of 2 mA cm−2, and even at a very high current rate of 50 mA cm−2, a reversible capacitance of 5.40 F cm−2 can still be retained after 1000 charge–discharge cycles. When the sample was employed as the cathode to build an asymmetric supercapacitor (ASC) with activated carbon as the anode, the device exhibited an areal capacitance of 1.26 F cm−2 at a current rate of 2 mA cm−2 and a coulombic efficiency of 97.7%. Furthermore, this device showed great potential for practical application by lighting up 8 red light-emitting diodes.

Graphical abstract: One-pot synthesis of self-supported hierarchical urchin-like Ni3S2 with ultrahigh areal pseudocapacitance

Article information

Article type
Paper
Submitted
30 ሜይ 2018
Accepted
10 ጁላይ 2018
First published
12 ጁላይ 2018

J. Mater. Chem. A, 2018,6, 22115-22122

One-pot synthesis of self-supported hierarchical urchin-like Ni3S2 with ultrahigh areal pseudocapacitance

Q. He, Y. Wang, X. X. Liu, D. J. Blackwood and J. S. Chen, J. Mater. Chem. A, 2018, 6, 22115 DOI: 10.1039/C8TA05050C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements