Selective metallization of alumina ceramics by inkjet printing combined with electroless copper plating

Abstract

A convenient and efficient approach for selective metallization of alumina ceramics has been developed. The Ag+-bearing ink was firstly inkjet-printed on alumina ceramics to create catalytic activating layers for subsequent electroless copper plating (ECP), and then ECP was initiated to fabricate the desirable conductive patterns. A continuous copper layer with dense packing could be obtained by controlling the electroless plating process. A low resistivity of about 2.37 μΩ cm of the copper layer was achieved, which was only about 1.4 times higher than that of bulk copper. Moreover, such a copper layer exhibited satisfactory solderability, reliable adhesion to substrates and good stability in an ambient atmosphere. This approach proposed a potential way to realize surface metallization on ceramic substrates without high temperature and any sophisticated equipment.

Graphical abstract: Selective metallization of alumina ceramics by inkjet printing combined with electroless copper plating

Article information

Article type
Paper
Submitted
02 ኦገስ 2016
Accepted
10 ኦክቶ 2016
First published
10 ኦክቶ 2016

J. Mater. Chem. C, 2016,4, 10240-10245

Selective metallization of alumina ceramics by inkjet printing combined with electroless copper plating

J. Chen, Y. Guo, Y. Wang, J. Zhang, H. Li and Z. Feng, J. Mater. Chem. C, 2016, 4, 10240 DOI: 10.1039/C6TC03315F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements