Alkali metals incorporated ordered mesoporous tantalum oxide with enhanced photocatalytic activity for water splitting

Abstract

Herein, we report a novel synthetic approach for the preparation of alkali (Na, K) metal incorporated ordered mesoporous tantalate composites and their photocatalytic performance for water splitting. With the main focus on sodium based composite materials, a series of samples with ordered mesoporosity and high surface area (108–120 m2 g−1) was prepared by a variation of the Ta/Na ratios through a soft templating route. The structural parameters and properties of the samples were analyzed by low angle XRD, N2-physisorption, TEM and STEM analysis, EDX, XPS, Raman and diffuse reflectance UV-Vis spectroscopy. The incorporation of alkali metals resulted in ordered mesoporous tantalate composites. Furthermore, the addition of alkaline earth (Ca, Ba, Sr) metals to the precursor solution of ordered mesoporous tantalum oxide was attempted. However, alkaline earth metals gave unordered tantalate composites. Photocatalytic investigations for water splitting, by using methanol as a sacrificial agent, indicated that the incorporation of alkali metals enhanced the hydrogen production rate of the photocatalyst whereas addition of alkaline earth metals decreased the hydrogen production. Among the sodium based samples, a Ta/Na ratio of 9 showed the best performance. The efficiency of this sample was further improved through decorated NiOx as co-catalyst. A 2.5 wt% NiOx loading was found to be the optimal loading amount, generating 64 μmol h−1 H2 and 31 μmol h−1 O2 when tested for overall water splitting.

Graphical abstract: Alkali metals incorporated ordered mesoporous tantalum oxide with enhanced photocatalytic activity for water splitting

Supplementary files

Article information

Article type
Paper
Submitted
06 ሴፕቴ 2015
Accepted
02 ኖቬም 2015
First published
02 ኖቬም 2015

J. Mater. Chem. A, 2016,4, 3007-3017

Author version available

Alkali metals incorporated ordered mesoporous tantalum oxide with enhanced photocatalytic activity for water splitting

T. Grewe and H. Tüysüz, J. Mater. Chem. A, 2016, 4, 3007 DOI: 10.1039/C5TA07086D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements