Synthesis of Na2SiF6:Mn4+ red phosphors for white LED applications by co-precipitation

Abstract

A one-step approach to synthesize Na2SiF6:Mn4+and K2SiF6:Mn4+ red phosphors by co-precipitation is reported in this paper. The phosphors were precipitated from a silicon fluoride solution with NaF and Na2MnO4 (Na2SiF6:Mn4+ preparation) or KF and K2MnO4 (K2SiF6:Mn4+ preparation) using H2O2 to reduce Mn7+ to Mn4+ at room temperature. Na2SiF6:Mn4+ was also prepared through a convenient two-step route with K2MnF6 as a raw material. The obtained Na2SiF6:Mn4+ phosphors have hexagonal structures with space group D32-P321 and no impurity phase when they were examined via X-ray diffraction. Photoluminescence, photoluminescence excitation, thermal luminescence, and luminescence decay time were considered to determine the optical properties of the fluoride complexes. The prepared phosphors exhibited bright red emission under 460 nm light excitation and low-thermal quenching (∼92% of the luminescent intensity at 423 K). Increasing the concentration of Mn4+ enhanced the luminescence intensity. A warm white light LED with high color rendering index (Ra = 86 and R9 = 61) was fabricated by employing Na2SiF6:Mn4+ as red phosphors and commercial Y3Al5O12:Ce3+ as yellow phosphors on a blue-InGaN chip.

Graphical abstract: Synthesis of Na2SiF6:Mn4+ red phosphors for white LED applications by co-precipitation

Supplementary files

Article information

Article type
Communication
Submitted
14 ሴፕቴ 2014
Accepted
01 ኦክቶ 2014
First published
02 ኦክቶ 2014

J. Mater. Chem. C, 2014,2, 10268-10272

Author version available

Synthesis of Na2SiF6:Mn4+ red phosphors for white LED applications by co-precipitation

H. Nguyen, C. C. Lin, M. Fang and R. Liu, J. Mater. Chem. C, 2014, 2, 10268 DOI: 10.1039/C4TC02062F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements