A comparative study on the NOx storage and reduction performance of Pt/Ni1Mg2Al1Ox and Pt/Mn1Mg2Al1Ox catalysts

Abstract

A series of Ni1Mg2Al1Ox, Mn1Mg2Al1Ox, 0.5Pt/Ni1Mg2Al1Ox and 0.5Pt/Mn1Mg2Al1Ox catalysts were carefully prepared and their NOx storage and reduction (NSR) performance including NOx oxidation efficiency (NOE), NOx storage capacity (NSC), NOx conversion rate (XNO), N2 selectivity (SN2), N2O selectivity (SN2O) and NH3 selectivity (SNH3), was systematically investigated. A SO2 resistance test was also performed in the presence of 100 ppm SO2. The NOE and NSC experimental results revealed that the Ni1Mg2Al1Ox catalyst possesses a higher NSC, while the Mn1Mg2Al1Ox catalyst possesses a better NOE. With regard to XNO, 0.5Pt/Ni1Mg2Al1Ox presented higher results at 200 °C and 400 °C, while 0.5Pt/Mn1Mg2Al1Ox obtained the highest result at 300 °C, which was more than 60% for both. In addition, compared to 0.5Pt/Ni1Mg2Al1Ox, 0.5Pt/Mn1Mg2Al1Ox exhibited a relatively higher SN2 and lower SN2O and SNH3. The NOx-TPD and H2-TPSR results indicated that NOx adsorbed on Ni1Mg2Al1Ox and 0.5Pt/Ni1Mg2Al1Ox is more stable, and that NH3 can be formed in large amounts in a lower temperature range. Both Pt-containing catalysts presented a quite stable XNO in ten cycles in the presence of 100 ppm SO2, and their SN2 can be remarkably enhanced to more than 80%, which could be attributed to the reactions of NH3-SCR and SO2 + NH3. We believe this new insight can provide a new way of thinking for the development of NSR catalysts.

Graphical abstract: A comparative study on the NOx storage and reduction performance of Pt/Ni1Mg2Al1Ox and Pt/Mn1Mg2Al1Ox catalysts

Article information

Article type
Paper
Submitted
24 Way 2019
Accepted
27 Dit 2019
First published
28 Dit 2019

Dalton Trans., 2020,49, 3970-3980

A comparative study on the NOx storage and reduction performance of Pt/Ni1Mg2Al1Ox and Pt/Mn1Mg2Al1Ox catalysts

C. Zhang, Y. Gao, N. Altaf and Q. Wang, Dalton Trans., 2020, 49, 3970 DOI: 10.1039/C9DT03787J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements