A novel one-pot methodology combining anionic polymerization and polyhomologation, through a “bridge” molecule (BF3OEt2), was developed for the synthesis of polyethylene (PE)-based block copolymers. The anionically synthesized macroanion reacts with the “bridge” molecule to afford a 3-arm star (trimacromolecular borane) which serves as an initiator for the polyhomologation.
By using functionalized ylides and/or organoboranes, functionalized linear and nonlinear homo/copolymers, such as α-hydroxyl-ω-allylic PE, 3-armed α-hydroxyl PE star, PE-co-PP(polypropylene) and cyclic PE have been synthesized.7 Until now, polyhomologation has been combined with controlled/living radical and ring opening polymerization reactions to afford PE-based block copolymers such as PS-b-PE, PEO-b-PE diblock and PE-b-PDMS-b-PE triblock copolymers, etc. (PS: polystyrene; PEO: polyethylene oxide; PDMS: polydimethylsiloxane).8
Here, we report a novel one-pot methodology combining anionic polymerization and polyhomologation, through a “bridge” molecule (BF3OEt2), for the synthesis of polyethylene (PE)-based block copolymers. The synthetic approach involves: (a) the synthesis of a 3-arm star polymer (trimacromolecular borane, macroinitiator) by reacting living macroanions with BF3OEt2, (b) the in situ polyhomologation of dimethylsulfoxonium methylide, with the macroinitiator to produce a 3-arm star block copolymer of PE, and (c) the oxidation/hydrolysis by trimethylamine N-oxide dihydrate (TAO) to afford the PE-based block copolymers. As examples the syntheses of PBd-b-PE (PBd: polybutadiene) and PS-b-PE are shown in Scheme 1. The details are given in the ESI.†
Scheme 1 Combination of anionic polymerization and polyhomologation leading to PBd-b-PE and PS-b-PE block copolymers (BF3OEt2: “bridge” molecule). |
A living macroanion, PBdLi or PSLi, was first synthesized in cyclohexane at room temperature and then reacted (30% excess) with BF3OEt2 (0.7 M solution in diethyl ether) to afford a 3-arm boron-linked star. Due to the high sensitivity of boranes to air (oxygen and moisture) it was not possible to analyse the stars formed by size exclusion chromatography (SEC), since the borane species decompose during analysis (Fig. 1). The peaks corresponding to the products of coupling of PBd and PS anions with BF3OEt2 almost disappeared after 24 and 18 hours, respectively, and thus the decomposition of these macromolecular boranes (2- and 3-arm stars) was confirmed.
Fig. 1 The products of coupling of PBd and PS anions with BF3OEt2 decompose during SEC measurements (THF at 35 °C). |
In order to avoid the decomposition, (PBd)3B and (PS)3B 3-arm stars were directly used after synthesis in situ for the polymerization of dimethylsulfoxonium methylide in toluene at 70 °C and 80 °C, respectively.
The dimethylsulfoxonium methylide (monomer) was prepared in refluxed tetrahydrofuran (THF) at 70 °C from trimethylsulfoxonium chloride in the presence of sodium hydride according to Corey's method (yield: 60–80%).9 After synthesis, THF was switched to toluene, the polymerization solvent.
The polyhomologation of dimethylsulfoxonium methylide with the star-like macroinitiators, (PBd)3B and (PS)3B, resulted in the corresponding 3-arm star block copolymers (PBd-b-PE)3B and (PS-b-PE)3B, which could not be analyzed by SEC due to reasons explained above. Oxidation/hydrolysis of the resulting starblock copolymers with trimethylamine N-oxide dihydrate (TAO) led to the linear ω-hydroxyl PBd-b-PE and PS-b-PE. Parallel experiments led to the conclusion that the methylide monomer cannot be polymerized either by the macroanion (PBdLi and PSLi) or by BF3OEt2. This indicates that only the boron-linked 3-arm star polymer has the potential for polyhomologation. The initiating efficiency of the different boron-based 3-arm stars depends on the chemical nature/steric hindrance of the arms. Macroinitiators based on polybutadiene initiate the polyhomologation much faster than PS3B. For example, polyhomologation leading to DP = 1700 could be completed in less than 10 min at 70 °C with (PBd)3B as an initiator, whereas one hour was needed when PS3B was used at 80 °C. After polyhomologation and cooling to room temperature, the toluene solution turned cloudy thus indicating successful formation of a PE block (Fig. 2).
Fig. 2 PS-b-PE solution in toluene after polyhomologation at 80 °C and 25 °C. |
The syntheses of PBd-b-PE and PS-b-PE were monitored by HT(high temperature)-SEC in trichlorobenzene (TCB) at 150 °C (Fig. 3). It is clear that the peak appearing after polyhomologation moves to the higher molecular weight region (lower elution volumes), the lower molecular weight peak corresponding to the excess precursor eliminated after fractionation. For this reason the polyhomologation products were dissolved in toluene at high temperature to give a clear and transparent solution, followed by cooling to room temperature. The solution was then centrifuged in the presence of a small amount of selective solvent for PBd (petroleum ether) and PS (acetone) to facilitate the separation. The absence of the PBd and PS precursors (Fig. 3) proves the success of the fractionation (Table 1).
Fig. 3 Syntheses of PBd-b-PE and PS-b-PE monitored by HT-SEC using TCB as an eluent at 150 °C. a The negative peak was shown with positive style for better comparison (dn/dc of PE and PBd are negative in TCB). |
Sample | PBd or PS block | PE block | (PBd or PS)-b-PE | |||||
---|---|---|---|---|---|---|---|---|
Mn (× 103) | PDIHT-SEC | Mn,theor. (× 103)c | Mn,NMR (× 103) | PDIHT-SEC | Tm (°C) | Tg (°C) | UCST (°C)g | |
a The molecular weight was determined by MALDI-ToF (Fig. S1, ESI).b The molecular weight was determined by HT-SEC using TCB as an eluent at 150 °C with a flow rate of 0.8 mL min−1 calibrated by PS standards.c The molecular weight was calculated from the ratio of the ylide to the initiator.d Mn,PE,NMR = 14 × DPPBd × (A0.8–2.4ppm − 0.6 × A6.9–7.4ppm − 2 × A4.8–5.6ppm)/A4.8–5.6ppm.e Mn,PE,NMR = 14 × DPPS × (A0.8–2.4ppm − 0.6 × A6.4–7.4ppm)/(2.5 × A6.4–6.8ppm).f The glass transition of the PS block was hidden by the melting process of the PE block.g Upper critical solution temperature (UCST) was measured in toluene (3 mg mL−1) on a UV-Vis instrument with a manual temperature controller. | ||||||||
PBd-b-PE | 5.9a | 1.05 | 10.5 | 24.0d | 1.14 | 101 | −85 | 40–55 |
PS-b-PE | 6.5b | 1.09 | 3.3 | 11.9e | 1.11 | 102 | —f | 40–55 |
Successful syntheses of diblock copolymers have been confirmed by Fourier-transformed infrared spectroscopy (FTIR) (Fig. 4). In the case of PBd-b-PE, the peaks at 964 and 910 cm−1 characteristic of and attributable to C–H bending vibration in PBd blocks were found.
Fig. 4 FTIR spectra of PBd-b-PE and PS-b-PE copolymers, aPE standard with a molecular weight of 2000. |
In the DSC curve (Fig. 5) of the PBd-b-PE diblock copolymer, a melt temperature of 101 °C attributable to the PE block was found, as well as the glass transition to the PBd block at ca. −85 °C. In the case of PS-b-PE, the glass transition of the PS block was covered by the melting process of the PE block.
Fig. 5 DSC curves of PBd-b-PE and PS-b-PE diblock copolymers. |
The PE fingerprint is clearly seen from the thermal behavior of the PE copolymers in toluene monitored by UV-Vis measurements at 450 nm. The graphs (transmittance as a function of temperature) of PBd-b-PE and PS-b-PE are shown in Fig. 6. A phase transition occurs at 40–55 °C upon heating the PBd-b-PE solution (3 mg mL−1): the transmittance then increases from ∼40% to 100%. For PS-b-PE, the phase transition is much more significant as the transmittance increases from 2% to 100% upon increasing the temperature to 40–55 °C.
Fig. 6 Thermal responses of PBd-b-PE and PS-b-PE copolymers revealed by 1H NMR in toluene-d8 (left) at different temperatures and UCST measurements in toluene (3 mg mL−1) (right). |
The PE fingerprint was also evident in the thermal responses (shielding effect) of diblock copolymers in 1H NMR spectra (Fig. 6). The single and sharp peak at 1.4 ppm, attributable to the protons in PE backbone, compared to vinyl protons in the 1,4-type double bond in the PBd block at 5.5 ppm, increases with temperature, which means that more and more PE blocks dissolved in the solvent. The area ratio of the peaks at 1.4 ppm to the one at 4.8–5.6 ppm was used to calculate the ratio of the PE block in the copolymers using: Mn,PE,NMR = 14 × DPPBd × (A0.8–2.4ppm − 0.6 × A6.9–7.4ppm − 2 × A4.8–5.6ppm)/A4.8–5.6ppm. Correspondingly, the peaks of aryl protons due to the PS blocks at 6.4–6.9 ppm were employed to calculate the respective contents of PS and PE in PS-b-PE copolymers. Surprisingly, the molecular weights calculated in this way were higher than expected. For PBd-b-PE, the molecular weight of 24.0 × 103 drawn from NMR for the PE block is 2.3 times higher than the expected value of 10.5 × 103. The deviation is more obvious for PS-b-PE (Table 1). The higher molecular weight observed indicates that the macroinitiator concentration was lower than the theoretical one, meaning that the efficiency of the linking reaction (living polymers with BF3OEt2) was about 30%. Other reasons for this disagreement in molecular weights should be excluded since the PDIs of the final block copolymers were very low (Table 1).
In conclusion, a novel strategy, based on anionic polymerization combined with polyhomologation through a “bridge” molecule (BF3OEt2), has been proposed for the synthesis of PE-based block copolymers. The examples described in this work (PBd-b-PE and PS-b-PE) are only two out of the many that can be prepared by this general methodology. A few are given below: ABE, (AB)2or3CE, (ABC)2or3DE, ABCDE, (ABCD)2or3FE, etc. (A, B, C, D, E, F: different blocks, E: polyethylene). The potential of this method is limited only by our imagination.
Footnote |
† Electronic supplementary information (ESI) available: Experimental details and the MALDI-ToF mass spectrum of PBd. See DOI: 10.1039/c3cc44928a |