Additive manufacturing of barium-doped calcium silicate/poly-ε-caprolactone scaffolds to activate CaSR and AKT signalling and osteogenic differentiation of mesenchymal stem cells

Abstract

3D-printed scaffolds are suitable for patient-specific implant preparation for bone regeneration in large-scale critical bone defects. In addition, these scaffolds should have mechanical and biological properties similar to those of natural bone tissue. In this study, 3D-printed barium-doped calcium silicate (BaCS)/poly-ε-caprolactone (PCL) composite scaffolds were fabricated as an alternative strategy for bone tissue engineering to achieve appropriate physicochemical characteristics and stimulate osteogenesis. Scaffolds containing 10% Ba (Ba10) showed optimal mechanical properties, preventing premature scaffold degradation during immersion while enabling ion release in a sustained manner to achieve the desired therapeutic goals. In addition, Wharton's jelly mesenchymal stem cells (WJMSCs) were used to assess biocompatibility and osteogenic differentiation behaviour. WJMSCs were cultured on the scaffold and permeabilised via ICP to analyse the presence of Si and Ba ions in the medium and cell lysates, suggesting that the ions released by the scaffold could effectively enter the cells. The protein expression of CaSR, PI3K, Akt, and JNK confirmed that CaSR could activate cells cultured in Ba10, thereby affecting the subsequent PI3k/Akt and JNK pathways and further promoting osteogenic differentiation. The in vivo performance of the proposed scaffolds was assessed using micro-CT and histological slices, which revealed that the BaCS scaffolds could further enhance bone regeneration, compared with bare scaffolds. These results suggest the potential use of 3D-printed BaCS/PCL scaffolds as next-generation substitutes for bone regeneration.