Precise size separation of water-soluble red-to-near-infrared-luminescent silicon quantum dots by gel electrophoresis†
Abstract
Gel electrophoresis, which is a standard method for separation and analysis of macromolecules such as DNA, RNA and proteins, is applied for the first time to silicon (Si) quantum dots (QDs) for size separation. In the Si QDs studied, boron (B) and phosphorus (P) are simultaneously doped. Codoping induces a negative potential on the surface of a Si QD and makes it dispersible in water. Si QDs with different B and P concentrations and grown at different temperatures (950 °C–1200 °C) are studied. It is shown that native polyacrylamide gel electrophoresis can separate codoped Si QDs by size. The capability of gel electrophoresis to immobilize size-separated QDs in a solid matrix makes detailed analyses of size-purified Si QDs possible. For example, the photoluminescence (PL) studies of the dried gel of Si QDs grown at 1100 °C demonstrate that a PL spectrum of a Si QD solution with the PL maximum around 1.4 eV can be separated into more than 15 spectra with the PL maximum changing from 1.2 to 1.8 eV depending on the migration distance. It is found that the relationship between the PL peak energy and the migration distance depends on the growth temperature of Si QDs as well as the B and P concentration. For all the samples with different impurity concentrations and grown at different temperatures, a clear trend is observed in the relationship between the full width at half maximum (FWHM) and the peak energy of the PL spectra in a wide energy range. The FWHM increases with the increasing peak energy and it is nearly twice larger than those observed for undoped Si QDs. The large PL FWHM of codoped Si QDs suggests that excitons are further localized in codoped Si QDs due to the existence of charged impurities.