Hydrogen-induced structural transformation of AuCu nanoalloys probed by synchrotron X-ray diffraction techniques†
Abstract
In situ X-ray diffraction measurements reveal that the transformation of a AuCu nanoalloy from a face-centered-cubic to an L10 structure is accelerated under a hydrogen atmosphere. The structural transformation rate for the AuCu nanoalloy under hydrogen above 433 K was found to be 100 times faster than that in a vacuum, which is the first quantitative observation of hydrogen-induced ordering of nanoalloys.