Glass transition of poly(methyl methacrylate) nanospheres in aqueous dispersion

Abstract

Surfactant-free nanospheres and latex nanospheres of poly(methyl methacrylate) (PMMA) with diameter ranging from 20 to 220 nm are prepared by atom transfer radical polymerization (ATRP) in microemulsions and subsequent dialysis against deionized water. The glass transitions of these PMMA nanospheres are characterized using nano differential scanning calorimetry (nano-DSC) in aqueous dispersions. The glass transition temperature (T_g) of the surfactant-free PMMA nanospheres and nonionic PMMA latex nanospheres with diameters below 150 nm is less than that of the PMMA bulk, and T_g decreases with the decrease of the diameter. In contrast, T_g of the anionic PMMA latex nanospheres is size-independent and is near to that of the PMMA bulk. The influence of the environment surrounding the PMMA nanospheres on glass transitions as well as comparisons to our prior studies with polystyrene (PS) nanospheres in aqueous dispersions are discussed.