Electromechanical response and failure behaviour of aerogel-spun carbon nanotube fibres under tensile loading

Abstract

The effect of tensile loading on the mechanical and electrical behaviour of carbon nanotube fibres spun continuously from an aerogel is discussed. While these fibres exhibit moderate strength (0.19 GPa) and elastic moduli (9.16 GPa), their piezoresistive behaviour, evaluated through active resistance measurements during tensile loading, demonstrates their potential for sensing applications in advanced composite materials. Insight into the failure behaviour of the aerogel-spun fibres is gained through microscopic examination of the failed fibres, as well as analysis of their electrical response. A new phenomenon for carbon nanotube fibres is reported—the aerogel-spun fibres are observed to undergo mild to severe kinking due to tensile failure. This kinking is attributed to compressive failure due to recoil from the fibre free ends. A simple analysis of experimental results yields a fibre compressive strength range of 172–177 MPa.

Graphical abstract: Electromechanical response and failure behaviour of aerogel-spun carbon nanotube fibres under tensile loading

Article information

Article type
Paper
Submitted
14 Nov 2011
Accepted
25 Jan 2012
First published
27 Feb 2012

J. Mater. Chem., 2012,22, 6792-6798

Electromechanical response and failure behaviour of aerogel-spun carbon nanotube fibres under tensile loading

A. S. Wu, T. Chou, J. W. Gillespie, D. Lashmore and J. Rioux, J. Mater. Chem., 2012, 22, 6792 DOI: 10.1039/C2JM15869H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements