Reported are the synthesis and the structural characterization of the new ternary antimonides Eu7Ga8Sb8, Sr7Ga8Sb8, Ba7Ga8Sb8, and Ba7In8Sb8. They have been synthesized from reactions of the corresponding elements, using gallium or indium as metal fluxes. The four compounds are isostructural and crystallize with the space group P63/mmc (no. 194) with lattice parameters as follows: a = 4.4942(8), c = 17.274(6) Å for Eu7Ga8Sb8; a = 4.5409(8), c = 17.486(4) Å for Sr7Ga8Sb8; a = 4.7045(12), c = 18.123(9) Å for Ba7Ga8Sb8; and a = 4.8274(3), c = 18.421(2) Å for Ba7In8Sb8. The temperature dependence of the magnetic susceptibility of Eu7Ga8Sb8 confirms that the Eu ions are in the typical divalent state (Eu2+) with a room temperature effective magnetic moment μeff = 8.02 μB. A phase transition from a paramagnetic to an antiferromagnetically ordered structure occurs in this material below 6 K. These results are corroborated by 151Eu Mössbauer spectroscopy at 4.2 and 78 K, respectively. Eu7Ga8Sb8, Ba7In8Sb8 and the previously reported Sr7Ga2Sb6 derivative of the cubic Th3P4 type, were also investigated by 121Sb Mössbauer spectroscopy.
You have access to this article
Please wait while we load your content...
Something went wrong. Try again?