Highly efficient mesoporous-composite electrodes were made by a doctor-blade technique from nano-sized SnO2 and submicron-sized ZnO. Coating pastes were prepared by mixing colloidal SnO2 or powdered SnO2 nanoparticles with ZnO submicron particles in the presence of acetic acid, acetylacetone, Triton X-100, and a cellulose thickener. The thickness of SnO2/ZnO-composite electrodes was controlled from 2.6 to 22 µm. The paste using colloidal SnO2 nanoparticles gave SnO2-covered ZnO submicron-sized particles, leading to a high conversion efficiency of the dye-sensitized solar cells (DSCs) at a thickness of 8.8 µm (Voc
= 721 mV, Jsc
= 12.41 mA cm−2, FF
= 0.709 and η
= 6.34%). On the other hand, the use of powdered SnO2 nanoparticles resulted in the formation of mixed large aggregates which were isolated from each other, giving low conversion-efficiency solar cells. The existence of a thin Zn2+ layer on the SnO2 layer of the composite electrode is proposed to explain the improvement in the DSC parameters.
You have access to this article
Please wait while we load your content...
Something went wrong. Try again?