Physical and photocatalytic properties of sprayed Dy doped ZnO thin films under sunlight irradiation for degrading methylene blue

Abstract

Dysprosium-doped zinc oxide (ZnO) thin films have been prepared through spray pyrolysis onto glass substrates. Cross-sections of the deposited thin films were assessed through Scanning Electron Microscopy (SEM), showing thicknesses between 200 and 300 nm. The thin film roughness was evaluated using the obtained images from the Atomic Force Microscope (AFM) micrographs. The crystallographic structure of the samples was analyzed by X-ray diffraction (XRD) revealing polycrystalline thin films. However, the slight shift towards a higher 2θ angle in Dy-doped ZnO films as compared to the pure ones indicates the incorporation of Dy³⁺ into the ZnO crystal lattice. The analysis of the oxidation state via X-ray photoelectron spectroscopy (XPS) confirms the incorporation of Dy ions in the ZnO matrix. Besides, UV-Vis-NIR spectrophotometry analysis and photoluminescence (PL) spectroscopy showed that bandgap energy values of ZnO decreased when dysprosium doping increased. Therefore, Dy doped ZnO thin films can be potentially used as a solar-light-driven photocatalyst. Among the different doping yields, the ZnO doped with 6% dysprosium provides the highest degradation rate for methylene blue (MB) under solar irradiation. Specifically, 9% of dye degradation was achieved under sunlight irradiation for 120 minutes.