Thin cyclomatrix polyphosphazene films: interfacial polymerization of hexachlorocyclotriphosphazene with aromatic biphenols

Author affiliations

Abstract

A series of thin cyclomatrix polyphosphazene films has been prepared by interfacial polymerization of hexachlorocyclotriphosphazene (HCCP) with an aromatic biphenol. The pKa values of the biphenol used strongly influence the properties of the hyper-cross-linked films formed. 4,4′-Dihydroxybiphenyl (BPH) and 4,4′-dihydroxydiphenyl ether (DHPE) possess pKa values in the range of 9.4–9.6 & 10.0–10.3 for the mono- and di-ionized forms, respectively, and produce films with a lower cross-link density, whereas 4,4′-dihydroxybenzophenone (DHBP) and 4,4′-sulfonyldiphenol (BPS) feature lower pKa values (7.4–7.6 & 8.0–8.2), resulting in films with a higher cross-link density. The difference in cross-link density is reflected in, e.g., the surface morphology and mechanical properties of the films. Mechanical stiffness has been quantitatively assessed by PeakForce QNM AFM. Lower cross-link densities result in Young's moduli with average values of 44–69 MPa, with a sharp distribution, while higher cross-link densities yield broadly distributed Young's moduli with average values of 255–306 MPa, depending on the choice of the biphenol. The surface chemistry of the films was successfully altered by post-functionalization.

Graphical abstract: Thin cyclomatrix polyphosphazene films: interfacial polymerization of hexachlorocyclotriphosphazene with aromatic biphenols

Back to tab navigation

Publication details

The article was received on 21 Mar 2018, accepted on 14 May 2018 and first published on 17 May 2018


Article type: Paper
DOI: 10.1039/C8PY00444G
Citation: Polym. Chem., 2018,9, 3169-3180
  •   Request permissions

    Thin cyclomatrix polyphosphazene films: interfacial polymerization of hexachlorocyclotriphosphazene with aromatic biphenols

    E. Maaskant, H. Gojzewski, M. A. Hempenius, G. J. Vancso and N. E. Benes, Polym. Chem., 2018, 9, 3169
    DOI: 10.1039/C8PY00444G

Search articles by author

Spotlight

Advertisements