Kinetic analysis for cyclic CO2 capture using lithium orthosilicate sorbents derived from different silicon precursors

Abstract

A series of Li4SiO4 was synthesized using LiNO3 and six different silicon precursors. The precipitated-silica-derived Li4SiO4 presented the highest CO2 capacity in a 10 h sorption test, and ZSM-5-derived Li4SiO4 demonstrated the most rapid CO2 sorption. The CO2 sorption kinetics predominantly followed the nucleation mode and could be accurately described by the Avrami-Erofeev model. The Avrami-Erofeev model provided an in-depth analysis of correlation between sorption performance and material properties. Both the nucleation speed and nucleation dimensionality affected the overall sorption kinetics. The kinetics and pore-size distribution suggest that the sorption kinetics was dependent on the quantity of ∼4 nm-pores which favors nucleation dimensionality. For the cyclic tests, the precipitated-silica-derived sample presented the poorest performance with the capacity decreasing from 31.33 wt% at the 1st cycle to only 11.52 wt% at the 30th cycle. However, the sample made from fumed silica displayed an opposite trend with the capacity increasing from 19.90 wt% at the 1st cycle to 34.23 wt% at the 30th cycle. The radically distinct behaviour of samples during cycles was on account of the alternation of sorption kinetics. The decrease in ∼4 nm-pores after cycles was responsible for the decrease of nucleation dimensionality for the precipitated-silica-derived sample. The rearrangement during cycles could enrich the pores of ∼4 nm for the fumed silica-derived sample, which improved the nucleation growth, thus enhancing the kinetics with cycles.

Graphical abstract: Kinetic analysis for cyclic CO2 capture using lithium orthosilicate sorbents derived from different silicon precursors

Supplementary files

Article information

Article type
Paper
Submitted
23 Apr 2018
Accepted
10 Jun 2018
First published
11 Jun 2018

Dalton Trans., 2018,47, 9038-9050

Kinetic analysis for cyclic CO2 capture using lithium orthosilicate sorbents derived from different silicon precursors

M. Zhao, H. Fan, F. Yan, Y. Song, X. He, M. Z. Memon, S. K. Bhatia and G. Ji, Dalton Trans., 2018, 47, 9038 DOI: 10.1039/C8DT01617H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements