Ladder-like polysilsesquioxane dielectrics for organic field-effect transistor applications

Author affiliations

Abstract

A series of trimethylsilyl-capped hybrid ladder-like polysilsesquioxane (LPSQ-TMS) derivatives were synthesized comprising an inorganic backbone functionalized with various organic side moieties and compositional ratios with application towards gate dielectrics or surface modifying materials. The surface energy (γ) and roughness (Rq) values of the LPSQ-TMS coated SiO2 dielectrics were considerably affected by the side moieties of the polymer series; methyl, n-propyl, phenyl (P), naphthyl (N), methacryloxypropyl (MA), and fluorooctyl moieties. The γ values varied from 17.0 to 42.0 mJ m−2, while the Rq values also ranged from 0.34 to 1.10 nm. On polymer-treated SiO2 dielectrics possessing smooth and semiconductor-compatible surface properties, pentacene developed terrace-like crystallites formed through layer-by-island growth modes, a stark contrast to the three-dimensionally grown crystal islands formed on rough or extremely hydrophobic surfaces, which led to unfavorable conduction pathways. Depending on the order of conjugation and interconnections between the pentacene domains, the average mobility (μFET) values of the resulting 50 nm thick pentacene organic field-effect transistors were varied by two orders of magnitude and reached 0.8 cm2 V−1 s−1, specifically, for both the P- and MA-substituted LPSQ-TMS treated SiO2 dielectrics (γ = 37.0 mJ m−2 and Rq = 0.40 nm). Moreover, we were able to demonstrate that a thermally cured 500 nm thick LPSQ-TMS layer on an Au gate-patterned flexible polyimide substrate could yield pentacene OFETs with μFET values as high as 0.60 cm2 V−1 s−1, comparable to that of the LPSQ-TMS treated SiO2 system. Also, the proper introduction of organic substituents to LPSQ improved the gate-bias stress stability for high performance OFETs.

Graphical abstract: Ladder-like polysilsesquioxane dielectrics for organic field-effect transistor applications

Back to tab navigation

Supplementary files

Publication details

The article was received on 23 May 2017, accepted on 11 Sep 2017 and first published on 12 Sep 2017


Article type: Paper
DOI: 10.1039/C7TC02278F
Citation: J. Mater. Chem. C, 2017,5, 10955-10964
  •   Request permissions

    Ladder-like polysilsesquioxane dielectrics for organic field-effect transistor applications

    M. Pei, A. S. Lee, S. S. Hwang and H. Yang, J. Mater. Chem. C, 2017, 5, 10955
    DOI: 10.1039/C7TC02278F

Search articles by author

Spotlight

Advertisements