Synthesis of well-defined epoxy-functional spherical nanoparticles by RAFT aqueous emulsion polymerization

Author affiliations

Abstract

The environmentally-friendly synthesis of epoxy-functional spherical nanoparticles has been achieved using polymerization-induced self-assembly (PISA) in aqueous solution. Firstly, a non-ionic hydrophilic stabilizer block, poly(glycerol monomethacrylate) (PGMA), was prepared by reversible addition–fragmentation chain transfer (RAFT) solution polymerization in ethanol. This water-soluble precursor was subsequently chain-extended via RAFT aqueous emulsion polymerization of glycidyl methacrylate (GlyMA) at 50 °C and neutral pH to ensure maximum retention of the epoxy functionality. PISA leads to the formation of well-defined PGMA-PGlyMA spherical diblock copolymer nanoparticles at up to 35% w/w solids and 1H NMR spectroscopy studies indicated that virtually all of the epoxy groups survive such relatively mild conditions. DMF GPC studies confirmed that relatively low dispersities (Mw/Mn < 1.30) were obtained if the mean degree of polymerization of the core-forming PGlyMA block remained below 100. Well-defined triblock copolymer nanoparticles could also be prepared via seeded RAFT emulsion polymerization of n-butyl methacrylate, with DMF GPC analysis indicating a relatively narrow molecular weight distribution (Mw/Mn < 1.20). The epoxy groups within the nanoparticle cores were ring-opened by adding sodium azide to a 10% w/w aqueous copolymer dispersion at 50 °C, as confirmed by FT-IR spectroscopy. PGMA45-PGlyMA100 diblock copolymer nanoparticles could be conveniently converted into cationic nanogels by utilizing water-soluble diamines as crosslinkers. These nanogels were characterized by DLS and aqueous electrophoresis and remained intact when dispersed in DMF; in contrast, the corresponding linear precursor nanoparticles dissociated to form molecularly-dissolved copolymer chains under the same conditions.

Graphical abstract: Synthesis of well-defined epoxy-functional spherical nanoparticles by RAFT aqueous emulsion polymerization

Back to tab navigation

Supplementary files

Publication details

The article was received on 04 Jul 2017, accepted on 22 Jul 2017 and first published on 27 Jul 2017


Article type: Paper
DOI: 10.1039/C7PY01107E
Citation: Polym. Chem., 2017, Advance Article
  •   Request permissions

    Synthesis of well-defined epoxy-functional spherical nanoparticles by RAFT aqueous emulsion polymerization

    F. L. Hatton, J. R. Lovett and S. P. Armes, Polym. Chem., 2017, Advance Article , DOI: 10.1039/C7PY01107E

Search articles by author

Spotlight

Advertisements