Design of the nanoarray pattern Fe–Ni bi-metal nanoparticles@M13 virus for the enhanced reduction of p-chloronitrobenzene through the micro-electrolysis effect

Author affiliations

Abstract

Novel M13 virus-supported nanoarray patterns of bi-metal nanoparticles (NPs) were designed, synthesized and used for the enhanced reduction of p-chloronitrobenzene (p-CNB) based on the micro-electrolysis effect. Considering the potential difference between the non-noble metals Ni/Cu and Fe, FeNPs uniformly dispersed on the shaft surface of wild M13 (w-M13) were synthesized and designated as the anode and Ni/CuNPs as the cathode, with the filamentous M13 serving as the conductive “wire”. The assembled Fe–Ni@w-M13 and Fe–Cu@w-M13 micro-electrolysis systems were applied in p-CNB reduction. Compared with the single FeNPs, NiNPs and CuNPs with or without the supporting M13, both Fe–Ni@w-M13 and Fe–Cu@w-M13 exhibited an enhanced p-CNB reduction efficiency. Selecting Fe–Ni@w-M13 with the maximum p-CNB reduction ratio as the target, the reduction product of p-CNB was determined to be p-chloroaniline (p-CAN), and the oxidation product of the anode FeNPs was Fe(II). According to the optimal initial molar ratio (3 : 1) of Fe(II) : Ni(II) and TEM observation of Fe–Ni@w-M13, the quantity ratio of FeNPs to NiNPs on the surface of w-M13 was calculated to be approximately 2.4 : 1 through the pseudo crystal hypothesis. Engineered M13 (e-M13) with increased surface negative charges was further constructed, and the adsorption affinity of e-M13 toward Ni(II) was nearly 3-fold the affinity of w-M13 toward Ni(II). For Fe–Ni@e-M13, the ratio of FeNPs to NiNPs on the surface of e-M13 changed to 1.2 : 1; a higher p-CNB reduction efficiency was observed compared to Fe–Ni@w-M13, and the reduction rate constant was 1.87- and 2.68-fold those of Fe@e-M13 and FeNPs, respectively. With an optimal Fe–Ni@e-M13 dosage, 93% of p-CNB was rapidly reduced to p-CAN through the micro-electrolysis effect.

Graphical abstract: Design of the nanoarray pattern Fe–Ni bi-metal nanoparticles@M13 virus for the enhanced reduction of p-chloronitrobenzene through the micro-electrolysis effect

Back to tab navigation

Supplementary files

Publication details

The article was received on 04 Feb 2017, accepted on 10 Feb 2017 and first published on 13 Feb 2017


Article type: Paper
DOI: 10.1039/C7EN00120G
Citation: Environ. Sci.: Nano, 2017,4, 876-885
  •   Request permissions

    Design of the nanoarray pattern Fe–Ni bi-metal nanoparticles@M13 virus for the enhanced reduction of p-chloronitrobenzene through the micro-electrolysis effect

    S. Zhang, H. Yu, J. Yang and Z. Shen, Environ. Sci.: Nano, 2017, 4, 876
    DOI: 10.1039/C7EN00120G

Search articles by author

Spotlight

Advertisements