Low temperature conductivity and ion dynamics in silver iodide–silver metaphosphate glasses

Author affiliations

Abstract

Silver iodide–silver metaphosphate glasses xAgI·(1 − x)AgPO3 (x = 0.3, 0.4, and 0.5) have been prepared using the usual melt quenching method. Differential scanning calorimetry has been used to determine the glass transition temperature of the samples. Impedance spectroscopy spanning wide temperature (20 K to 200 K) and frequency (10−1 Hz to 106 Hz) ranges has been employed to investigate the ion dynamics. At high temperatures, below the glass transition temperature and down to around 120 K, the dynamics show the usual behavior of dc and dispersed conductivity due to the random and correlated motion of the ions. The dc conductivity of the glasses varies dramatically and it increases with the AgI content as expected. At the lowest temperatures investigated, however, the conductivity of the glasses was indistinguishable. Hence, the low temperature dynamics are identical irrespective of the amount of AgI and the structure of the glass. In addition, a nearly constant loss behavior, independent of the temperature and composition, was attained at the lowest temperatures.

Graphical abstract: Low temperature conductivity and ion dynamics in silver iodide–silver metaphosphate glasses

Back to tab navigation

Publication details

The article was received on 01 Jun 2017, accepted on 18 Jul 2017 and first published on 18 Jul 2017


Article type: Paper
DOI: 10.1039/C7CP03695G
Citation: Phys. Chem. Chem. Phys., 2017,19, 21527-21531
  •   Request permissions

    Low temperature conductivity and ion dynamics in silver iodide–silver metaphosphate glasses

    L. Badr, Phys. Chem. Chem. Phys., 2017, 19, 21527
    DOI: 10.1039/C7CP03695G

Search articles by author

Spotlight

Advertisements