Room temperature solvent-free reduction of SiCl4 to nano-Si for high-performance Li-ion batteries

Author affiliations

Abstract

SiCl4 can be directly reduced to nano-Si with commercial Na metal under solvent-free conditions by mechanical milling. Crystalline nano-Si with an average size of 25 nm and quite uniform size distribution can be obtained, which shows excellent lithium storage performance, for a high reversible capacity of 1600 mA h g−1 after 500 cycles at 2.1 A g−1.

Graphical abstract: Room temperature solvent-free reduction of SiCl4 to nano-Si for high-performance Li-ion batteries

Back to tab navigation

Supplementary files

Publication details

The article was received on 13 Apr 2017, accepted on 15 May 2017 and first published on 15 May 2017


Article type: Communication
DOI: 10.1039/C7CC02857A
Citation: Chem. Commun., 2017,53, 6223-6226
  •   Request permissions

    Room temperature solvent-free reduction of SiCl4 to nano-Si for high-performance Li-ion batteries

    Z. Liu, X. Chang, B. Sun, S. Yang, J. Zheng and X. Li, Chem. Commun., 2017, 53, 6223
    DOI: 10.1039/C7CC02857A

Search articles by author

Spotlight

Advertisements