Highly efficient CH3NH3PbI3−xClx mixed halide perovskite solar cells prepared by re-dissolution and crystal grain growth via spray coating

Author affiliations

Abstract

We fabricated highly efficient planar type CH3NH3PbI3−xClx (MAPbI3−xClx) mixed halide perovskite solar cells via spray coating with a controlled composition of the solvents. The cells had a power conversion efficiency of 17.8% (forward scan), 18.3% (reverse scan), and 16.08 ± 1.28% (average) for unit cells under 1 Sun conditions. We controlled the ratio of DMF (dimethylformamide), a quickly evaporating solvent, and GBL (γ-butyrolactone), a slowly evaporating solvent, to 10 : 0, 9 : 1, 8 : 2, and 7 : 3 (vol : vol). We obtained the largest MAPbI3−xClx mixed halide perovskite crystal grains in the 8 : 2 sample because the inward flux of the spray solution was balanced with the outward flux of the evaporating solvent. Consequently, the moistened underlying polycrystalline perovskite film with small crystal grains re-dissolved and merged into larger crystalline grains by re-crystallization. By controlling the re-dissolution and crystal grain growth of the MAPbI3−xClx mixed halide perovskite film via spray coating, we fabricated a sub-module (10 cm × 10 cm, active area = 40 cm2) with 10.5 V open circuit voltage, 84.15 mA short circuit current, 70.16% fill factor, and 15.5% power conversion efficiency under 1 Sun conditions.

Graphical abstract: Highly efficient CH3NH3PbI3−xClx mixed halide perovskite solar cells prepared by re-dissolution and crystal grain growth via spray coating

Back to tab navigation

Supplementary files

Publication details

The article was received on 05 Aug 2016, accepted on 20 Sep 2016 and first published on 20 Sep 2016


Article type: Communication
DOI: 10.1039/C6TA06718B
Citation: J. Mater. Chem. A, 2016,4, 17636-17642
  •   Request permissions

    Highly efficient CH3NH3PbI3−xClx mixed halide perovskite solar cells prepared by re-dissolution and crystal grain growth via spray coating

    J. H. Heo, M. H. Lee, M. H. Jang and S. H. Im, J. Mater. Chem. A, 2016, 4, 17636
    DOI: 10.1039/C6TA06718B

Search articles by author

Spotlight

Advertisements