Zr and Y co-doped perovskite as a stable, high performance cathode for solid oxide fuel cells operating below 500 °C

Author affiliations

Abstract

Zr and Y co-doped perovskite BaCo0.4Fe0.4Zr0.1Y0.1O3−δ (BCFZY0.1) was recently developed as a promising new cathode for protonic ceramic fuel cells (PCFCs). Here, it is applied for the first time as a cathode for low-temperature solid oxide fuel cells (LT-SOFCs). It exhibits large lattice parameters, high oxygen reduction reaction (ORR) activity, exceptional low-temperature performance, long-term stability, and excellent chemical compatability with ceria-based SOFC electrolytes. When BCFZY0.1 is used as the cathode in Ce0.8Gd0.2O2−δ (GDC20)-based SOFCs, it enables a peak power density of 0.97 W cm−2 at 500 °C with 2500 hours stable performance and complete recoverability without any degradation after more than 80 fast thermal ramping cycles. Even at 350 °C, peak power density reaches 0.13 W cm−2. It also shows good H2O and CO2 tolerance.

Graphical abstract: Zr and Y co-doped perovskite as a stable, high performance cathode for solid oxide fuel cells operating below 500 °C

Back to tab navigation
Please wait while Download options loads

Supplementary files

Publication details

The article was received on 04 Jul 2016, accepted on 07 Oct 2016 and first published on 07 Oct 2016


Article type: Paper
DOI: 10.1039/C6EE01915C
Citation: Energy Environ. Sci., 2017,10, 176-182
  •   Request permissions

    Zr and Y co-doped perovskite as a stable, high performance cathode for solid oxide fuel cells operating below 500 °C

    C. Duan, D. Hook, Y. Chen, J. Tong and R. O'Hayre, Energy Environ. Sci., 2017, 10, 176
    DOI: 10.1039/C6EE01915C

Search articles by author