3D Hetero-architecture of GdB6 nanoparticles on lessened cubic Cu2O nanowires: enhanced field emission behaviour†
Abstract
The field emission properties (FE) of a heteroarchitecture comprised of gadolinium hexaboride nanoparticles uniformly decorated over Cu2O nanoneedles (GdB6/Cu2O) have been investigated at the base pressure of ~1 × 10−8 mbar. Under the optimized pulsed laser deposition (PLD), a well-adhered coating of GdB6 nanoparticles on chemically synthesized cuprous oxide (Cu2O) nanoneedles has been obtained. A plausible growth mechanism of the hierarchical assembly of GdB6 nanoparticles on the Cu2O nanoneedles is explained on the basis of structural analysis carried out using SEM and TEM. A low turn-on field of ~2.3 V μm−1 (to draw an emission current density ~1 μA cm−2) is observed along with stable emission current at the preset value of ~2 μA over 4 h. The enhanced emission behaviour of the GdB6/Cu2O heteroarchitecture, in contrast to the pristine Cu2O nanoneedles, is attributed to its high aspect ratio and low work function. The observed FE results demonstrate GdB6/Cu2O heteroarchitecture as a potential candidate for application in various vacuum nano/microelectronic devices.