Precision Marangoni-driven patterning

Author affiliations


A Marangoni flow is shown to occur when a polymer film possessing a spatially-defined surface energy pattern is heated above its glass transition to the liquid state. This can be harnessed to rapidly manufacture polymer films possessing prescribed height profiles. To quantify and verify this phenomenon, a model is described here which accurately predicts the formation, growth, and eventual dissipation of topographical features. The model predictions, based on numerical solutions of equations governing thin film dynamics with a Marangoni stress, are quantitatively compared to experimental measurements of thin polystyrene films containing photochemically patterned surface energy gradients. Good agreement between the model and the data is achieved at temperatures between 120 and 140 °C for a comprehensive range of heating times using reasonable physical properties as parameter inputs. For example, thickness variations that measure 102% of the starting film thickness are achieved in only 12 minutes of heating at 140 °C, values that are predicted by the model are within 6% and 3 min, respectively. The photochemical pattern that directed this flow possessed only a 0.2 dyne cm−1 variation in surface tension between exposed and unexposed regions. The physical insights from the validated model suggest promising strategies to maximize the aspect ratio of the topographical features and minimize the processing time necessary to develop them.

Graphical abstract: Precision Marangoni-driven patterning

Back to tab navigation

Supplementary files

Publication details

The article was received on 13 Jun 2014, accepted on 07 Aug 2014 and first published on 07 Aug 2014

Article type: Paper
DOI: 10.1039/C4SM01284D
Citation: Soft Matter, 2014,10, 8043-8050
  •   Request permissions

    Precision Marangoni-driven patterning

    T. A. Arshad, C. B. Kim, N. A. Prisco, J. M. Katzenstein, D. W. Janes, R. T. Bonnecaze and C. J. Ellison, Soft Matter, 2014, 10, 8043
    DOI: 10.1039/C4SM01284D

Search articles by author