Bimetallic molybdenum tungsten oxynitride: structure and electrochemical properties
Abstract
Mesoporous molybdenum tungsten oxynitride was synthesised by the temperature-programmed reduction of the bimetallic
Maintenance work is planned from 09:00 BST to 12:00 BST on Saturday 28th September 2024.
During this time the performance of our website may be affected - searches may run slowly, some pages may be temporarily unavailable, and you may be unable to access content. If this happens, please try refreshing your web browser or try waiting two to three minutes before trying again.
We apologise for any inconvenience this might cause and thank you for your patience.
* Corresponding authors
a
Institute for Frontier Materials (IFM), Deakin University, Waurn Ponds 3216, VIC, Australia
E-mail:
alexey.glushenkov@deakin.edu.au
Fax: +61 3 5227 1103
Tel: +61 3 5227 2931
b
School of Physics and Centre for Research on Adaptive Nanostructures and Nanodevices (CRANN), Trinity College Dublin, Dublin 2, Ireland
E-mail:
hozhang@tcd.ie
Fax: +353 1 896 3033
Tel: +353 1 896 4655
Mesoporous molybdenum tungsten oxynitride was synthesised by the temperature-programmed reduction of the bimetallic
O. Kartachova, A. M. Glushenkov, Y. Chen, H. Zhang and Y. Chen, J. Mater. Chem. A, 2013, 1, 7889 DOI: 10.1039/C3TA10836H
This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.
Read more about how to correctly acknowledge RSC content.
Fetching data from CrossRef.
This may take some time to load.
Loading related content