The origin of high efficiency in low-temperature solution-processable bilayer organometal halide hybrid solar cells

Abstract

This work reports a study into the origin of the high efficiency in solution-processable bilayer solar cells based on methylammonium lead iodide (CH₃NH₃PbI₃) and [6,6]-phenyl-C₆₁-butyric acid methyl ester (PC₆₁BM). Our cell has a power conversion efficiency (PCE) of 5.2% under simulated AM 1.5G irradiation (100 mW cm⁻²) and an internal quantum efficiency of close to 100%, which means that nearly all the absorbed photons are converted to electrons and are efficiently collected at the electrodes. This implies that the exciton diffusion, charge transfer and charge collection are highly efficient. The high exciton diffusion efficiency is enabled by the long diffusion length of CH₃NH₃PbI₃ relative to its thickness. Furthermore, the low exciton binding energy of CH₃NH₃PbI₃ implies that exciton splitting at the CH₃NH₃PbI₃/PC₆₁BM interface is very efficient. With further increase in CH₃NH₃PbI₃ thickness, a higher PCE of 7.4% could be obtained. This is the highest efficiency attained for low temperature solution-processable bilayer solar cells to date.