Thermoelectric composites of poly(3-hexylthiophene) and carbon nanotubes with a large power factor

Author affiliations

Abstract

Composite films of poly(3-hexylthiophene) and single- as well as multi-walled carbon nanotubes are demonstrated to offer a competitive thermoelectric performance. The power factor significantly exceeds values obtained with either constituent alone provided that the conjugated polymer is sufficiently p-doped. The use of single-walled carbon nanotubes consistently results in a higher electrical conductivity with a maximum value above 103 S cm−1 and thus gives rise to a power factor of 25 ± 6 μW m−1 K−2 for a filler content of only 8 wt% and a maximum 95 ± 12 μW m−1 K−2 for 42–81 wt%. Moreover, a carbon nanotube content of 8–10 wt% does not compromise the low bulk thermal conductivity of the polymer matrix, which promises a high figure of merit of at least ZT > 10−2 at room-temperature. All samples are cast on plastic substrates, emphasising their suitability for large-area, flexible thermoelectric applications.

Graphical abstract: Thermoelectric composites of poly(3-hexylthiophene) and carbon nanotubes with a large power factor

Back to tab navigation

Supplementary files

Publication details

The article was received on 07 Sep 2012, accepted on 18 Dec 2012 and first published on 24 Jan 2013


Article type: Paper
DOI: 10.1039/C2EE23406H
Citation: Energy Environ. Sci., 2013,6, 918-925
  •   Request permissions

    Thermoelectric composites of poly(3-hexylthiophene) and carbon nanotubes with a large power factor

    C. Bounioux, P. Díaz-Chao, M. Campoy-Quiles, M. S. Martín-González, A. R. Goñi, R. Yerushalmi-Rozen and C. Müller, Energy Environ. Sci., 2013, 6, 918
    DOI: 10.1039/C2EE23406H

Search articles by author

Spotlight

Advertisements