Solid state 29Si NMR studies of apatite-type oxide ion conductors

Author affiliations

Abstract

Apatite-type silicates have been attracting considerable interest as a new class of oxide ion conductor, whose conduction is mediated by interstitial oxide ions. We report here the first 29Si solid state NMR studies of these materials with a systematic investigation of thirteen compositions. Our results indicate a correlation between the silicon environment and the observed conductivity. Specifically, samples which show poor conductivity demonstrate a single NMR resonance, whereas fast ion conducting compositions show more complex NMR spectra. For the oxygen excess samples La9M(SiO4)6O2.5 (M = Ca, Sr, Ba) two peaks are observed at chemical shifts of ≈−77.5 and −80.5 ppm, with the second peak correlated with a silicate group adjacent to an interstitial oxygen site. On Ti doping to give La9M(SiO4)6−x(TiO4)xO2.5 (x = 1,2) the second peak disappears, which is consistent with the “trapping” of interstitial oxygens by Ti and the consequent lowering in oxide ion conductivity. The samples La9.33(SiO4)6O2 and La9.67(SiO4)6O2.5 show a further third weak peak at a chemical shift (≈−85.0 ppm) consistent with the presence of some [Si2O7]6− units in these samples, due to condensation of two [SiO4]4− units. The effect of such condensation of [SiO4]4− units will be the creation of additional interstitial oxide ion defects, i.e. 2 [SiO4]4− → [Si2O7]6− + Oint2−. Overall, the results further highlight the importance of the [SiO4]4− substructure in these materials, and additionally suggest that 29Si NMR could potentially be used to screen apatite silicate materials for oxide ion conductivity

Graphical abstract: Solid state 29Si NMR studies of apatite-type oxide ion conductors

Back to tab navigation

Publication details

The article was received on 05 Jan 2006, accepted on 10 Feb 2006 and first published on 17 Feb 2006


Article type: Paper
DOI: 10.1039/B600122J
Citation: J. Mater. Chem., 2006,16, 1410-1413
  •   Request permissions

    Solid state 29Si NMR studies of apatite-type oxide ion conductors

    J. E. H. Sansom, J. R. Tolchard, M. S. Islam, D. Apperley and P. R. Slater, J. Mater. Chem., 2006, 16, 1410
    DOI: 10.1039/B600122J

Search articles by author

Spotlight

Advertisements