Navaladian Subramanian,
Balasubramanian Viswanathan* and
Thirukkallam K. Varadarajan
Department of Chemistry, National Centre for Catalysis Research, Indian Institute of Technology Madras, Chennai 600 036, India. E-mail: bvnathan@iitm.ac.in; Tel: +91 44 2257 4241
First published on 23rd July 2014
Potassium-birnessite (K-OL-1) samples of different morphologies (nanowire networks, nanoparticles and mesoporous hierarchical nanowire networks) and textural properties were synthesized from KMnO4 by using oxalate-reduction method under ambient conditions. Cryptomelane (K-OMS-2) samples of similar morphologies were synthesized by the calcination of birnessite samples. The synthesized MnO2 samples were characterized by XRD, TGA, DTA, SEM, TEM, nitrogen adsorption–desorption and ICP-OES analyses. One each of the birnessite and the cryptomelane samples showed mesoporous nature (pore size ∼50 Å and 66 Å respectively). The pH of the reaction medium has been found to have a key role in the properties of the resulting MnO2 samples. Electrochemical studies of MnO2–carbon black composites were performed in 0.1 M aqueous Na2SO4 solution using cyclic voltammetry and galvanostatic charge–discharge cycling. One of the birnessite samples with nanowire network morphology and a BET surface area of 202 m2 g−1 exhibited a high capacitance value of 234 F g−1. Electrochemical studies revealed that the specific capacitance values of the studied MnO2 materials have a direct relationship with their BET surface area values. Birnessite samples have exhibited better capacitance behavior and values than their cryptomelane derivatives. The effect of the morphology has also been reflected in the values of the specific capacitance.
Manganese oxides are important and well-studied class of materials in the fields of catalysis, ion-exchangers, molecular adsorption, biosensors, batteries, electrochemical capacitors, oxygen reduction (in fuel cells) and solar materials.12–19 Due to the low cost and that MnO2 forms variety of structures, MnO2-based materials have been anticipated as potential replacement for hydrous RuO2. The simple electrochemical double layer capacitance (EDLC) process is a non-Faradaic process attributed to charge separation at the electrode/electrolyte interface whereas the pseudocapacitive (Faradaic) process depends on redox reactions that occur in the bulk of the electrode materials as well. Hence, pseudocapacitors exhibit higher capacitance than the EDLC.3 There have been two mechanisms proposed to explain the charge storage behavior of MnO2 as an active electrode material in aqueous electrochemical supercapacitor.20 The first mechanism is based on the surface adsorption of protons (H+) or electrolyte cations (M+) on MnO2 (eqn (1)) and the second one involves the intercalation of protons (H+) or alkali metal cations (M+) such as Na+ in the bulk of the material upon reduction or deintercalation upon oxidation (eqn (2)).21,22 The first mechanism is predominant in the case of amorphous MnO2 materials whereas the second mechanism is predominant in the case of crystalline MnO2 materials.
(MnO2)surface + M+ + e− ⇆ (MnO2−M+)surface | (1) |
MnO2 + M+ + e− ⇆ MnOOM | (2) |
Hence, capacitance of MnO2 depends on crystal structure, ionic conductivity, size of the cavity (of tunnel and layers), morphology and textural properties such as surface area, pore size and pore volume.23–26 So, open structures of MnO2 such as layered and tunneled ones are more preferred for the fast ionic transportation into the bulk of the electrode material in order to achieve high capacitance.
MnO2 exists in several crystallographic forms such as α-, β-, γ-, δ-, λ- and ε-type, because the basic unit [MnO6] octahedron links in different ways. In particular, δ-, α-MnO2 and OMS-5 forms are of much interest in view of their good electrochemical capacitance behavior due to their large cavity and high ionic conductivity.23,25,27 Hence, synthesis of birnessite (δ-MnO2) and cryptomelane (α-MnO2) with the requisite features for showing high charge storage is of great interest. Birnessite is a layered manganese oxide material comprising layers of edge-shared MnO6 octahedra, and cations (A = K+, Na+) and water molecules situated between the negatively charged layers. These materials are known as octahedral layers (A-OL-1) with the interlayer cation (A+).28 Cryptomelane is a type of manganese oxide consisting of 2 × 2 edge-shared MnO6 octahedra chains, which are corner-connected to form one-dimensional tunnels of ca. 4.6 × 4.6 Å and the tunnels are stabilized by K+ ions.29 Also, the cryptomelane is known as octahedral molecular sieve (K-OMS-2). Schematic structures of K-birnessite and cryptomelane are given in Fig. 1. Potassium-birnessite can be converted into cryptomelane by heat treatment as depicted in Fig. 1.29
There has been a variety of methods known for the synthesis of birnessite and it has been synthesized by oxidizing Mn2+ by oxygen in presence of KOH, hydrothermal route, or calcination of KMnO4.30–33 Apart from those methods, chemical reduction of KMnO4 by using reducing agent such as ethanol, glucose, ascorbic acid, fumaric acid, maleic acid, ethylene glycol, or polyvinyl alcohol for obtaining birnessite has also been reported.22,28,34–36 Cao et al. reported the formation of an amorphous manganese oxide (AMO) by randomly mixing KMnO4 and oxalic acid solutions.37 However, strategic synthesis of birnessites with different morphologies and porosities by varying the rate and the order of mixing of the reactants, KMnO4 and oxalic acid, has not yet been known. This article describes the synthesis of birnessite with three different morphologies and textural properties by the alteration of rate and order of mixing KMnO4 and oxalic acid solutions, their further transformation to cryptomelane of similar morphologies by calcination, and their electrochemical performances for charge storage in 0.1 M aqueous Na2SO4 electrolyte.
Manganese and potassium contents in K–MnO2 samples were analyzed by inductively coupled plasma-optical emission spectra (ICP-OES) using PERKIN-ELMER OPTIMA 5300 DV ICP-OES system. Samples were dissolved in 1% HCl and emission of K and Mn was monitored at 766.49 nm and 257.6 nm respectively. Average oxidation state (AOS) of Mn was determined using a two-step procedure described previously.38 The samples were dissolved in H2SO4 solution and Mn3+ as well as Mn4+ was reduced to soluble Mn2+ using Fe2+. Titrations of the resulting Mn2+ and the excess of Fe2+ were carried out to determine the AOS. Scanning electron micrographs were recorded using FEI QUANTA FEG 200 scanning electron microscope operating at 30 kV. Transmission electron micrographs (TEM) were recorded with PHILIPS CM12 and JEOL-3010 transmission electron microscopes operating at 100 kV and 300 kV respectively. Samples for TEM analyses were prepared by dispersing them in ethanol by sonication followed by drop-drying on copper grids coated with carbon film.
Electrochemical performance of MnO2–ketjen black carbon composites was studied using cyclic voltammetry curves and charge–discharge curves. Ketjen black carbon was used as a conducting additive. Fabrication of electrodes for electrochemical studies was done as follows. In a typical procedure, 75 wt% of MnO2, 20 wt% of ketjen black EC-600 JD and 5 wt% of polyvinylidene fluoride (PVDF) were mixed by mild grinding. From the mixture, 10 mg of solid mass was taken and dispersed in 0.25 ml of doubly distilled water in a vial by ultrasonication. From the colloid, a volume of 10 μl was transferred to polished glassy carbon surface and dried at 60 °C to get the semisolid of the composite for electrochemical studies. Electrochemical studies were performed in 50 ml of 0.1 M aqueous sodium sulphate solution. Cyclic voltammograms were recorded at a scan rate of 10 mV s−1 in the potential range of 0 to 1 V and galvanostatic charge–discharge cycles were collected with a current of 0.5 mA. The cyclic voltammetry and galvanostatic charge–discharge experiments were performed using a CHI 660A (CH Instruments, USA) electrochemical work station. A conventional three-electrode cell consisting of a polished glassy carbon (GC) (0.07 cm2) working electrode, a Pt foil (5 cm2) counter electrode and a Ag/AgCl (Satd. KCl) reference electrode was used for the electrochemical studies of MnO2–carbon composites.
![]() | ||
Fig. 2 Powder XRD patterns of birnessites and cryptomelanes and A, B or C denotes the method of preparation. (a) Birnessite; (b) Crypt-400(2h); (c) Crypt-400; (d) Crypt-600. |
Reflections of XRD pattern of cryptomelanes obtained by calcining birnessite samples at 400 °C for 4 h and 600 °C for 4 h are indexed to tetragonal body centered lattice with the space group I4/m and lattice constants a = 9.784 Å and c = 2.2863 Å (JCPDS no. 44-0141). However, birnessites calcined at 400 °C for 2 h show only a few reflections of cryptomelane as compared to Crypt-400 samples. This shows that the calcination for 2 h is not sufficient for the formation of cryptomelane, especially for Birn-A and Birn-C. As per the intensity of the XRD lines, the crystalline nature of cryptomelanes obtained by the calcination at 400 °C for 2 h is in the following order; Crypt-B > Crypt-A > Crypt-C. This observation implies that Birn-B is transformed into cryptomelane in a more facile manner than A and C analogues. This kind of easy phase transformation observed with Crypt-B400(2h) may be attributed to lower stability, which in turn attributed to the lesser potassium content in Birn-B.42 XRD patterns of cryptomelanes obtained by the calcination at 800 °C for 2 h are given in Fig. S1.† The presence of XRD lines corresponding to only cryptomelanes proves that no further phase transition occurred even by the calcination at 800 °C for 2 h. The XRD results prove that the cryptomelanes synthesized by this method are thermally stable even at 800 °C.
![]() | ||
Fig. 3 TGA (A) and DTA (B) profiles of birnessite samples recorded in air atmosphere. (a) Birn-A; (b) Birn-B; (c) Birn-C. |
The average oxidation state (AOS) of manganese and K:
Mn ratio of both birnessites and cryptomelanes are given in Table 1. As for birnessites, the AOS of Mn is in the range of 3.68 to 3.81 and Birn-B shows the highest AOS. A similar trend is observed in the case of cryptomelanes as well. These values imply the presence of both Mn(IV) and Mn(III) ions in both birnessites and cryptomelanes.33 However, the AOS is found to be slightly higher for cryptomelanes. This increase in the AOS of Mn is attributed to the oxidation of residual Mn(III) to Mn(IV) during the calcination in air atmosphere at 400 °C. The K
:
Mn ratios of Birn-A, Birn-B and Birn-C are in the range of 0.1 to 0.14. This observation with potassium content of birnessite samples has good correlation with XRD and TGA results where Birn-B is revealed to undergo phase transition at low temperatures than Birn-A and Birn-C. This lower K
:
Mn ratio might be due to the lower K
:
Mn of 1
:
1 in KMnO4 precursor. It is known from the literature that only 10% of the initial K+ was incorporated into MnO2 in the case of birnessites synthesized by the chemical reduction of KMnO4.45 The slightly lower K
:
Mn ratio of cryptomelane samples than their precursor birnessite samples is probably due to the loss of potassium that occurred during the calcination followed by washing with deionized water prior to the estimation by ICP analysis. This loss of K may be attributed to the expulsion of K+, which in turn due to the space shrinkage that takes place during the phase-transition of layered MnO2 to tunneled one.42
Sample | AOS | K/Mn | BET surface area (SSA) (m2 g−1) | t-Plot surface area (m2 g−1) | Pore volume (cm3 g−1) (BET) | Micro pore volume (cm3 g−1) (t-plot) | Pore size (Å) (BJH) | Specific capacitance (Cs) (F g−1) from CD curves | Cs/SSA F m−2 |
---|---|---|---|---|---|---|---|---|---|
Birn-A | 3.68 | 0.140 | 202 | 28 | 0.51 | 0.014 | 101 | 234 | 1.158 |
Birn-B | 3.81 | 0.099 | 133 | 18 | 0.33 | 0.0093 | — | 113 | 0.849 |
Birn-C | 3.72 | 0.126 | 186 | 14 | 0.22 | 0.0069 | 50 | 201 | 1.080 |
Crypt-A400 | 3.71 | 0.124 | 136 | 22 | 0.57 | 0.011 | 196 | 137 | 1.007 |
Crypt-B400 | 3.85 | 0.101 | 40 | 4.5 | 0.17 | 0.0021 | — | 33 | 0.825 |
Crypt-C400 | 3.76 | 0.113 | 130 | 15 | 0.22 | 0.0073 | 66 | 128 | 0.985 |
![]() | ||
Fig. 5 SEM images of cryptomelane samples. (a) Crypt-A400; (b) Crypt-B400; (c) Crypt-C400; (d) Crypt-C600. |
HRTEM images of Birn-A are given in Fig. 6. HRTEM images of two different magnifications in Fig. 6a and b show the presence of particles with gel-type (porous) or fluffy appearance. Lattice-resolved HRTEM image in Fig. 6c shows projecting nanofibers of thickness ∼3 nm with lattice fringes thickness of 6.2 Å. However, thickness of lattice fringes is not found to be uniform and varies from 6.2 to 7.6 Å.46 These lattice fringes correspond to the d001 of end centered monoclinic birnessite lattice. This observation indicates that MnO6 octahedral layers are seen across the nanofibers, which in turn implies that growth of nanofibers has occurred along (100) facet of the birnessite lattice. The observed variable d001 of lattice fringes implies the poor crystalline nature of birnessite as observed in XRD pattern. Even in a same nanofiber, d001 is not uniform throughout the fiber. This may be due to the non-uniform K+ ion incorporation in between the layers, which in turn may be due to lower K content in the material. Moreover, some of the nanofibers are found to contain as low as four layers.
![]() | ||
Fig. 6 HRTEM images of Birn-A. (a) and (b) low magnification and (c) lattice-resolved TEM images of Birn-A. |
TEM images of cryptomelane samples are given in Fig. 7. TEM image of Crypt-A400 given in Fig. 7(a) shows the bunch of nest-like nanorods network of cryptomelane. Thicknesses of the nanorods are in the range of 8 to 20 nm and the length is up to ∼1 μm. TEM image of Crypt-B400 show the presence of pseudo-spherical particles of size that is ranging from ∼15 nm to ∼60 nm. TEM image of Crypt-C400 in Fig. 7(c) and S4† shows porous gel-type network of nanorods. Projection of nanorods (shown with arrows) in the periphery of the nest-like aggregate is seen and thickness of those nanorods is ∼20 nm. SAED pattern recorded on the aggregates shows rings, which are indexable to (220), (310), (301), (411) and (521) reflections of cryptomelane lattice.
HRTEM images of Crypt-A600 are given in Fig. 8. Low magnification HRTEM image in Fig. 8a shows the presence of nanorods of length up to few μm and thickness of the nanorods varies from 5 to 50 nm. HRTEM image of an edge of a nanorod of Crypt-A600 and its lattice-resolved image (inset) are given shown in Fig. 8b. Thickness of the nanorod is around 48 nm and the d value of the lattice fringes is 4.9 Å. This d value corresponds to {200} planes of the cryptomelane, revealing that growth of the nanorod has occurred along [100]. TEM image in Fig. 8c shows edges of the nanorods of thickness of ∼42 nm. The lattice-resolved image in Fig. 8d depicts the edge of the nanorod and the corresponding lattice fringes show the d value of 7 Å. This d value reveals that the lattice fringes correspond to {110} planes of cryptomelane and indicates that growth direction of the nanorod is [110]. This contradictory observation found between two different nanorods regarding lattice alignment implies that nanorod growth occur along [100] or [110] direction. TEM images of Crypt-A600 given in Fig. S5† show bundles of nanorods. This type of bundling might arise from the side-on fusion of nanorods occurred by oriented attachment during the heat treatment.38,47
HRTEM images of Crypt-B600 are given in Fig. 9. Low magnification image in Fig. 9(a) shows nanoplates, short nanorods and spherical particles. Sizes of the nanoparticles are in the range of 15 to 60 nm. Fig. 9(b) shows a lattice-resolved image of a couple of nanoplates and thicknesses of the lattice fringes are 7 Å and 4.9 Å. These lattice fringes correspond to {110} and {200} respectively. This implies that top and basal planes of nanoplates are {001} plane of cryptomelane lattice. Lattice-resolved HRTEM image of the nanoparticle in Fig. 9(c) shows lattice fringes corresponding to d200 of cryptomelane.
![]() | ||
Fig. 9 HRTEM images of Crypt-B600. (a) Low magnification image; (b) and (C) lattice-resolved images of nanoplates and a nanoparticle respectively. |
![]() | ||
Fig. 10 Nitrogen adsorption–desorption isotherms of (a) Birn-A, (b) Birn-B and (c) Birn-C. Inset shows the BJH pore size distributions. |
![]() | ||
Fig. 11 Nitrogen adsorption–desorption isotherms of (a) Crypt-A400, (b) Crypt-B400, and (c) Crypt-C400. Inset shows BJH pore size distributions. |
As for BET surface area, the trend of cryptomelanes is similar to that of birnessite samples. In general, surface area calculated using t-plot is indicative of the surface area that arises due to micropores. Birn-A and Crypt-A400 exhibit microporous surface area of 28 and 22 m2 g−1 respectively, which are higher than that of B and C analogues of birnessite and cryptomelane. Microporous surface area of Birn-B decreased drastically when it was transformed to Crypt-B400. Microporous surface area of Birn-C is only 14 m2 g−1 and it is maintained even after the transformation into cryptomelane. Pore volume of Birn-A is higher than that of Birn-B and Birn-C due to the wide range of pore sizes exhibited by the former. Upon transition into Crypt-A400, the pore volume increases for Birn-A due to the increase in the pore size. However, in the case of both Birn-C and Crypt-C400, the pore volume remains the same even though the pore size increases from 50 to 66 Å. This phenomenon is mainly attributed to the effect of morphology. During sintering, crystallographically identical planes fuse (oriented attachment) to give rise to bigger particles and hence alignment of particles (or rods) is significant.38,47 The favorable alignment of the particles is less likely in the case of Birn-C because the nanorods are thickly packed, unlike Birn-A.47 Birn-B, on the contrary, show high degree of sinteing to form bigger particles due to its non-1 D morphology, that provides more freedom for favorable alignment than the rod morphology. In Fig. S7 and S8,† Horvath–Kawazoe micropore size distributions of birnessites and cryptomelanes are given as it is a reliable indicator of micropore size distribution of materials. The average micropore size lies below 10 Å for birnessites and cryptomelanes. The differences in the textural properties observed among cryptomelanes are mainly attributed to the morphology and the associated alignment of their birnessite precursor particles.
2KMnO4 + 3H2C2O4 → 2MnO2↓ + 6CO2↑ + 2KOH + 2H2O | (3) |
This reaction is more favorable even at room temperature due to the favorable standard reduction potentials of potassium permanganate and oxalic acid. The corresponding standard reduction potentials are Eo(MnO4−/MnO2−, 2OH−) = 1.679 V and Eo(2CO2/C2O42−) = −0.49 V.50,51 During the reaction, gas evolution was observed and the gas was tested by dipping the outlet of the reaction in baryta solution (10% Ba(OH)2 in water). Formation of white precipitate was observed while the outlet gas was purged through baryta, confirming the CO2 evolution from reaction medium to form BaCO3 (white precipitate).52 As understood from the eqn (3), pH of the solution after the completion of reaction was found to be alkaline (pH ≈ 9.6). In general, this reduction reaction is fast only in the acidic medium because H+ is consumed in this reaction.53 In addition, there was no reaction occurring when potassium oxalate was used in place of oxalic acid. After the reduction of MnO4− by oxalic acid, formation of MnOx is observed. Further, it polymerizes to form edge-shared MnO6 octahedral layers in the presence of K+ ions in neutral or acidic medium under mild conditions to form birnessites. Formation of crystalline birnessites occurs only in highly alkaline solutions at high temperature or under hydrothermal conditions.28,32,35,40,54,55 Hence, birnessite formed in the current synthesis is amorphous.
In order to understand the effect of pH, a separate set of experiments was carried out by measuring pH of reaction medium after 5 min of addition of every 10 ml of reactants. In method A, the initial pH of ∼3.4 was increasing gradually to 9.64 (after the complete addition). The colloid formation was observed only after addition of 40 ml of KMnO4 (pH ≈ 5.1). This implies that the nucleation and particle growth take place at acidic condition. Further, addition of KMnO4 generates MnOx units, which stack over the birnessite nuclei crystallite to give rise to the formation of fibers of birnessite. So is the case with method C except that the growth rate is faster in method C (due to the mixing of reactants all at once). Therefore, formation of thickly-packed nanorods (a gel-type) with uniform pore size has been observed. However, initial and final pH values were 8.7 and 9.6 respectively in the case of method B and pH has not reduced below 7.3 throughout the addition of oxalic acid. And, appearance of colloid was observed only after the addition of 80 ml (pH ≈ 8.1). This implies that homogenous nucleation followed by the fast particle growth occur in alkaline medium. Hence, formation of only non-spherical particles or plates is observed in the case of method B.20,28,32,53–55 Thus, pH plays a major role in the nucleation and the crystal growth and, in turn, in the morphology and the textural properties of the resulting MnO2. Cryptomelane samples synthesized retain the morphology and the nature of the pore size distribution of their birnessite precursor analogues. Based on the results, a schematic of formation of K–MnO2 material synthesized is presented in Fig. 12.
![]() | ||
Fig. 13 Cyclic voltammograms of birnessite (A) and cryptomelane (B) carbon composite electrodes, run in 0.1 M aqueous Na2SO4 solution at a scan rate of 10 mA s−1. |
Charge–discharge cycles of the carbon composites of birnessites and cryptomelanes are given in Fig. 14(A) and (B) respectively. The specific capacitance values of MnO2–carbon composites were calculated using the formula, C = I Δt/ΔVm, where, I is the current, Δt is discharge time of cycle, ΔV is potential window and m is mass of the composite.20,28,32,55 Linear variation of the charge–discharge curves is observed for the birnessite samples. Specific capacitance values of composites are given in Table 1. Specific capacitance of Ketjen black carbon measured under the similar conditions is only 13 F g−1. Specific capacitance of Birn-A, Birn-B and Birn-C is 234, 113 and 201 F g−1 respectively. The highest specific capacitance i.e., 234 F g−1, shown by Birn-A may be attributed to its highest surface area i.e., 202 m2 g−1. The specific capacitance of A, B and C of cryptomelane analogue is 137, 33 and 128 F g−1 respectively. In the case of cryptomelanes also, the same order of capacitance values holds good. In order to ignore the effect of surface area and look into other inherent contributing factors of the electrodes, ratio of specific capacitance (Cs) and specific surface area (SSA) has been calculated and given in Table 1. As for the ratios of Cs/SSA, a trend similar to that of specific capacitance is observed. In addition, the capacitance of the birnessites is found to be higher than that of cryptomelanes except that B (i.e., particles) analogues show similar values. The lower capacitance of Birn-B and Crypt-B400 may be due to their particle morphology which causes probably high electrode resistance. This observation has consistency with the poorly featured CV curve shown by B analogues. On the contrary, A and C analogues are nanowires (having long-range order in one dimension) and those nanowires are interconnected by forming network superstructure so higher conductivities are expected in their cases than B analogues (i.e., nanoparticles). In spite of the fact that electronic conductivity of the cryptomelane is higher than that of birnessites, birnessites show higher capacitance per unit surface area.25,62 Birnessite samples show better capacitance magnitudes than cryptomelanes even though the former is less crystalline than the latter as per XRD results. Although the crystalline nature of the Crypt-B400 and Crypt-C400 are higher than that of Crypt-A400 as understood from XRD line intensities, Crypt-A400 shows better capacitance values. These observations reveal that crystalline nature of MnO2 materials does not affect their capacitance significantly. Recently, Boisset et al., have studied the electrochemical performance of Na-Birnessite (synthesized) and cryptomelane (from Erachem-Comilog) electrodes in various lithium salts electrolytes including lithium sulphate using cyclic voltametry.63 It was found that cryptomelanes with the BET surface area of ∼218 m2 g−1 has shown a capacitance of ∼163 F g−1 in 2 M Li2SO4 and Na-birnessite with the BET surface area of ∼20 m2 g−1 has shown ∼185 F g−1 in the same electrolyte.63,64 Na-birnessite is found to show better capacitance performance than cryptomelane. Results of the current work are in consistent with those observations. Also, the MnO2 materials synthesized by the oxalate reduction method show better performances.
![]() | ||
Fig. 14 Galvanostatic charge–discharge curves of birnessite (A) and cryptomelane (B) carbon composite electrodes, run in 0.1 M aqueous Na2SO4 solution at a constant current of 0.5 mA. |
The observed capacitance values are in agreement with the argument that ionic conductivity is more essential than electronic conductivity for MnO2 in order for showing high capacity.25 In fact, ionic conductivity of birnessites is higher than that of cryptomelanes. The present study reveals that besides crystal structure, crystalline nature and surface area, ionic conductivity and morphology of the electrode materials are key factors in determining their capacitance values. Stability of the capacitance of the samples estimated based on the charge–discharge curves is provided in Fig. 15. Loss of capacitance after 1000 cycles for birnessites (A, B and C) is 6, 7.9 and 5.5% and for cryptomelanes (A, B and C) is 6.7, 12.1 and 6.1%, respectively. Stability results of the K–MnO2 samples imply that these samples show good stability and that birnessite samples show better stability than cryptomelane samples. In the case of both birnessites and ctyptomelanes, capacitance values for A and C analogues are more stable than B analogues. This might be due to the particle morphology of the B analogues. The better stability exhibited by the C analogues over the A analogues might be due to the rigid, hierarchical superstructure (formed with nanowires network) of the former. Hence, birnessites (A and C) synthesized by the current method can be promising and cost-effective materials for capacitor applications.
Electrochemical capacitance of MnO2–carbon black composites has been studied by CV curves and charge–discharge cycling. The specific capacitance values of MnO2 samples were found to have a direct relation with their specific surface area. One of the birnessite samples showed a specific capacitance (Cs) as high as 234 F g−1 and exhibit better capacitance behavior than its cryptomelane counterpart. Nanowires of MnO2 exhibited higher capacitance than nanoparticles. Thus, the present study suggests that textural properties, crystal structure, morphology and ionic conductivity govern the capacitance of MnO2-based electrode materials. These MnO2-based electrodes showed good stability over 1000 charge–discharge cycles. Thus, the present study suggests that Birn-A and Birn-C can be the cost-effective and promising electrode materials for capacitors.
Footnote |
† Electronic supplementary information (ESI) available: XRD powder patterns of Crypt-(A, B and C) 800(2h), SEM image and EDS of Crypt-C600, TEM image of Crypt-C400 and Crypt-A600, low angle XRD powder pattern of Birn-C and Horvath–Kawazoe pore size distributions of birnessite and cryptomelane samples. See DOI: 10.1039/c4ra05227g |