Synthesis of mesoporous silica spheres under quiescent aqueous acidic conditions

Abstract

A gyroid-to-sphere shape transition has been unveiled in the growth of mesoporous silica morphologies that are synthesized under quiescent acidic aqueous conditions. It can be induced by a decrease of the acidity for a surfactant-based gyroid preparation. As the acidity is gradually lowered from the gyroid domain, the growth process changes from one involving a smooth continuous deposition of silicate–surfactant micellar solute species onto specific regions of an evolving silicate liquid crystal seed, to one in which deposition instead occurs on non-specific regions of the seed. This creates multigranular gyroid morphologies which at lower acidity emerge as sphere shapes. The gyroid-to-sphere metamorphosis appears to correlate with an acidity and/or temperature dependent switch in the mode of formation, from the gyroid involving fast and local polymerization of a growing silicate liquid crystal seed, to the sphere based upon a slower and global polymerization of a silicate liquid crystal droplet. Surface tension will cause such a droplet to adopt a spherical shape, ultimately to be rigidified in the form of a mesoporous silica sphere. Comparative gyroid and sphere information is presented on synthesis-size-shape-channel plan relations, degree of orientational order of the channels, extent of polymerization of the silica, thermal stability and nitrogen adsorption properties. The ability to synthesize 1–10 µm diameter mesoporous silica spheres with a narrow sphere size and pore size distribution portends a myriad of applications in large molecule catalysis, chromatographic separations and nanocomposites.

References

1. H. Yang, N. Coombs and G. A. Ozin, Nature (London), 1997, 386, 692.
2. G. A. Ozin, H. Yang, I. Sokolov and N. Coombs, Adv. Mater., 1997, 9, 662.
3. H. Yang, A. Kuperman, N. Coombs, N. Mamiche-Afara and G. A. Ozin, Nature (London), 1996, 379, 703.
4. G. A. Ozin, D. Khushalani and H. Yang, in Proceedings of the NATO Advanced Research Workshop on ‘Molecular Recognition’, ed. J. Wuest, Val Morin, May 1996, Kluwer Academic Publications, Dordrecht, in press.
5. H. Yang, N. Coombs, I. Sokolov and G. A. Ozin, J. Mater. Chem., 1997, 7, 1285.
6. H. Yang, N. Coombs, I. Sokolov and G. A. Ozin, Nature (London), 1996, 381, 589.
7. H. Yang, N. Coombs, Ö. Dag, I. Sokolov and G. A. Ozin, J. Mater. Chem., 1997, 7, 1755.
8. H. Yang, N. Coombs and G. A. Ozin, Adv. Mater., 1997, 9, 811.
9. N. Coombs, D. Khushalani, S. Oliver, G. A. Ozin, G. C. Shen, I. Sokolov and H. Yang, J. Chem. Soc., Dalton Trans., 1997, 3941.
10. C. T. Kresge, M. E. Leonowicz, W. J. Roth, J. C. Vartuli and J. C. Beck, Nature (London), 1992, 359, 710.
11. J. S. Beck, J. C. Vartuli, W. J. Roth, M. E. Leonowicz, C. T. Kresge, K. T. Schmitt, C. T.-W. Chu, D. H. Olson, E. W. Sheppard, S. B. McCullen, J. B. Higgins and J. L. Schlenker, J. Am. Chem. Soc.., 1992, 114, 10 834.
12. F. Di Renzo, H. Cambon and R. Dutartre, Microporous Mater., 1997, 10, 283 history behind the discovery of the surfactant-based synthesis of periodic mesoporous silica.^10,11.
13. S. Mann and G. A. Ozin, Nature (London), 1996, 382, 313.
14. Q. Huo, J. Feng, F. Schüth and G. D. Stucky, Chem. Mater., 1997, 9, 14.
15. M. Grün, I. Lauer and K. K. Unger, Adv. Mater., 1997, 9, 254.
16. (a) I. A. Aksay, M. Trau, S. Manne, I. Honma, N. Yao, L. Zhou, P. Fenter, P. M. Eisenberger and S. M. Gruner, Science, 1996, 273, 892; (b) H. W. Hillhouse, T. Okubo, J. W. van Egmond and M. Tsapatsis, Chem. Mater., 1997, 9, 1505.
17. M. Ogawa, J. Am. Chem. Soc., 1994, 116, 7941.
18. M. Ogawa, Chem. Commun., 1996, 1149.
19. Y. Lu, R. Ganguli, C. A. Drewien, M. T. Anderson, C. J. Brinker, W. Gong, Y. Guo, H. Soyez, B. Dunn, M. H. Huang and J. I. Zink, Nature (London), 1997, 389, 364.
20. (a) Schacht, Q. Huo, I. G. Voigt-Martin, G. D. Stucky and F. Schüth, Science, 1996, 273, 768; (b) S. H. Tolbert, T. E. Schäffer, J. Feng, P. K. Hansma and G. D. Stucky, Chem. Mater., 1997, 9, 1962.
21. (a) H.-P. Lin and C.-Y. Mou, Science, 1996, 273, 765; (b) M. R. Raimondi, T. Maschmeyer, R. H. Templer and J. M. Seddon, Chem. Commun., 1997, 1843; (c) M. Trav, N. Yao, E. Kim, Y. Xia, G. M. Whitesides and I. A. Aksay, Nature (London), 1997, 390, 674.
22. E. Matijevic, Curr. Opin. Colloid Interface Sci., 1996, 1, 176 and references therein.
23. E. Matijevic, Pure Appl. Chem., 1988, 60, 1479.
24. C. J. Brinker and G. W. Scherer, Sol-Gel Science, Academic Press, San Diego, CA, 1990.
25. M. A. Bulter, P. F. James and J. D. Jackson, J. Mater. Sci., 1996, 31, 1675.
26. H. Izutsu, F. Mizukami, P. K. Nair, Y. Kiyozumi and K. Maeda, J. Mater. Chem., 1997, 7, 767.
27. L. C. Klein and R. H. Woodman, in Sol-Gel Science and Technology, ed. E. J. A. Pope, S. Sakka and L. C. Klein, The American Ceramic Society, Westerville, OH, 1995, pp. 105–116.
28. B. Karmakar, G. De, D. Kundu and D. Ganguli, J. Non-Cryst. Solids, 1991, 135, 29.
29. T. Tanev and T. J. Pinnavaia, Science, 1995, 267, 865.
30. A. Bagshaw, E. Prouzet and T. J. Pinnavaia, Science, 1995, 269, 1242.
31. A. Firouzi, F. Atef, A. G. Oertli, G. D. Stucky and B. F. Chmekla, J. Am. Chem. Soc., 1997, 119, 3596.
32. A. Steel, S. W. Carr and M. W. Anderson, Chem. Mater., 1995, 7, 1829.
33. S. J. Gregg and K. S. W. Sing, Adsorption, Surface Area and Porosity, Academic Press, London, 2nd edn., 1982, p. 113.
34. D. Dollimore and G. R. Heal, J. Appl. Chem., 1964, 14, 109.
35. Chemical Waves and Patterns, ed. R. Kapral and K. Showalter, Kluwer Academic, Dordrecht, The Netherlands, 1995.
36. S. T. Hyde, Curr. Opin. Solid StateMater. Sci., 1996, 1, 653.
37. R. K. Iler, The Chemistry of Silica, John Wiley & Sons, New York, 1979, pp. 180–189.
38. Q. Huo, D. I. Margolese, U. Ciesla, D. G. Demuth, P. Feng, T. E. Gier, P. Sieger, A. Firouzi, B. F. Chmekla, F. Schuth and G. D. Stucky, Chem. Mater., 1994, 6, 1176.